通过拉伸性能和冲击韧性试验及显微组织观察分析了厚板生产线控制轧制(CR)后采用超快冷(UFC)和层流冷(AcC)两种冷却工艺对AH32高强船板力学性能、焊接热影响区(HAZ)冲击韧性和显微组织的影响.结果表明,与AcC钢板相比UFC钢板性能明显提高,其屈服强度提高54 MPa且塑性不恶化,-60℃冲击功达到260 J以上,韧脆转变温度大幅降低.UFC使钢的显微组织明显细化,晶粒尺寸达到11.5级,且厚度方向显微组织更均匀,而AcC钢晶粒尺寸为9.5级.UFC对钢的焊接热模拟试样冲击韧性没有明显影响.用铁素体(α)形核动力学和Hall-Petch效应分析了晶粒细化机理及对强韧性影响.UFC降低了奥氏体(γ)转变温度,提高了α形核速率而细化了铁素体晶粒,同时也细化了贝氏体和珠光体,明显提高了钢的力学性能.
参考文献
| [1] | DeArdo A J .Accelerated cooling:a physical metallurgy perspective[J].Canadian Metallurgical Quarterly,2013,27(2):141-154.,2013. |
| [2] | Ouchi C .Development of steel plates by intensive use of TMCP and direct quenching processes[J].ISIJ International,2001,41(6):542-553.,2001. |
| [3] | 王国栋.新一代控制轧制和控制冷却技术与创新的热轧过程[J].东北大学学报（自然科学版）,2009(07):913-922. |
| [4] | Hodgson P,Beladi H,Barnett M R .Grain refinement in steels through thermomechanical processing[J].Materials Science Forum,2005,500 |
| [5] | Tomida T,Imai N,Miyata K,et al .Grain refinement of C-Mn steel to 1 μm by rapid cooling and short interval multi-pass hot rolling in stable austenite region[J].ISIJ International,2008,48(8):1115-1148.,2008. |
| [6] | Nobuo S,Shinji M,Shigeru E.Recent development in microstructural control technologies through the thermo-mechanical control process (TMCP) with JFE steel's high-performance plates[J].JFE Technical Report,2008 (11):1-6.,2008. |
| [7] | Kagechika H .Production and technology of iron and steel in Japan during 2005[J].ISIJ International,2006,46(7):939-958.,2006. |
| [8] | Ichimiya K,Sumi H,Hirai T.460 MPa-yield-strength-class steel plate with JFE EWEL (C) technology for large-heat-input welding[J].JFE Technical Report,2008 (11):7-12.,2008. |
| [9] | Nishimura K,Matsui K,Tsumura N.High performance steel plates for bridge construction[J].JFE Technical Report,2005(5):30-36.,2005. |
| [10] | 王国栋新一代TMCP的实践和工业应用举例[J].上海金属,2008,30(3):1-4.WANG Guo-dong.Practice and industry applications for the new generation TMCP[J].Shanghai Metals,2008,30(3):1-4.,2008. |
| [11] | 周晓光,王猛,刘振宇,吴迪,王国栋.超快冷对X70管线钢组织和性能的影响[J].材料热处理学报,2013(09):80-84. |
| [12] | 王新,陈小林,田士平,等 .超快冷技术在首秦宽厚板生产线上的应用[J].钢铁研究学报,2011,23(1):11-14.WANG Xin,CHEN Xiao-lin,TIAN Shi-ping,et al.Development and application of ultra fast cooling technology on heavy plate production line[J].Journal of Iron and Steel Research,2011,23(1):11-14.,2011. |
| [13] | 卢敏,周晓光,刘振宇,王国栋,狄国标.冷却工艺对X80级抗大变形管线钢组织性能的影响[J].材料热处理学报,2011(07):83-88. |
| [14] | 李凡,衣海龙,陈军平,刘振宇,王国栋.超快冷技术在鞍钢Q55o工程机械用钢生产中的应用[J].轧钢,2011(05):7-8,50. |
| [15] | 康健,王昭东,王国栋,袁国,周晓光.建筑用高强度低屈强比钢板的冷却工艺[J].材料热处理学报,2010(11):79-84. |
| [16] | 狄国标,周砚磊,姜中行,刘振宇,麻庆申.轧后冷却工艺对海洋平台用钢组织性能的影响[J].材料热处理学报,2011(10):56-61. |
| [17] | 蔡庆伍,唐获,徐福昌,李谋渭,李成果,王润生,高亮,丛津功.中厚板在线控冷高密度管层流水冷装置的开发[J].钢铁,2001(04):66-69,78. |
| [18] | 中国船级社材料与焊接规范[M].北京:人民交通出版社,2012.,2012. |
| [19] | Imao T .Some fundamental steps in thermomechanical processing of steels[J].Transactions ISIJ,1987,27(10):763-779.,1987. |
| [20] | Gladman T.The Physical Metallurgy of Microalloyed Steels[M].London:The Institute of Materials,1997.,1997. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%