为获得较低的黏度、较好流动性以及高固相含量的陶瓷浆料,采用同轴圆筒旋转黏度计,测试了不同配方双峰级配电熔刚玉粉体浆料的表观黏度,研究了粉体粒径、颗粒形貌以及级配比例对浆料流动性和固相含量的影响规律.研究表明:粗细颗粒的大粒径比、规则球形、宽粒度分布有利于制备低黏度高固相含量的陶瓷浆料.成功制备了表观黏度仅为0.411 Pa·s、固相含量为63％的陶瓷浆料,制备的陶瓷铸型在1 300℃下的强度大干18 MPa,烧成收缩率小于1％.
参考文献
| [1] | 李涤尘,吴海华,卢秉恒.型芯型壳一体化空心涡轮叶片制造方法[J].航空制造技术,2009(03):38-42. |
| [2] | H. Wu;D. Li;Y. Tang;N. Guo;F. Cui;B. Sun .Rapid casting of hollow turbine blades using integral ceramic moulds[J].Proceedings of the Institution of Mechanical Engineers, Part B. Journal of engineering manufacture,2009(6):695-702. |
| [3] | Smith PA.;Haber RA. .EFFECT OF PARTICLE PACKING ON THE FILTRATION AND RHEOLOGY BEHAVIOR OF EXTENDED SIZE DISTRIBUTION ALUMINA SUSPENSIONS[J].Journal of the American Ceramic Society,1995(7):1737-1744. |
| [4] | 许海仙,丘泰,杨建,郭坚.DMAA凝胶体系凝胶注模成型超细ZrO2陶瓷[J].无机材料学报,2011(10):1105-1110. |
| [5] | 王宇华,高利敏,张富强.凝胶注模氧化锆陶瓷浆料颗粒级配研究[J].临床口腔医学杂志,2012(09):527-529. |
| [6] | 徐斌,赵巍,周彩楼,白戈俊,王希婷.凝胶注模成型氧化铝陶瓷反射体的制备[J].电子元件与材料,2012(05):15-17. |
| [7] | J. KOLCZYK;J. ZYCH .RHEOLOGICAL PROPERTIES OF CERAMIC SLURRIES WITH COLLOIDAL BINDERS USED IN THE INVESTMENT CASTING TECHNOLOGY[J].Metalurgija,2013(1):55-58. |
| [8] | 王峰,谢志鹏,贾翠,千粉玲,孙加林,郝洪顺.高性能氮化硅陶瓷凝胶注模成型的研究[J].人工晶体学报,2011(03):743-747. |
| [9] | 刘炜;杨金龙;董英鸽 等.颗粒级配对凝胶注模成型氧化铝陶瓷的影响[J].人工晶体学报,2009,8(38):211-214. |
| [10] | MORI T;INAMINE I;WADA R et al.Effects of particle concentration and additive amount of dispersant on adsorption behavior of dispersant to alumina particles[J].Journal of the Ceramic Society of Japan,2009,117(1368):917-921. |
| [11] | FARRIS R J .Prediction of the viscosity of multimodal suspensions from unimodal viscosity data[J].Transactions of the Society of Rheology,1968,12(02):281-301. |
| [12] | Kuide Qin;Abbas A.Zaman .Viscosity of concentrated colloidal suspensions:comparison of bidisperse models[J].Journal of Colloid and Interface Science,2003(2):461-467. |
| [13] | 张立明 .陶瓷悬浮液流变特性及胶态成型坯体缺陷的控制[D].北京:清华大学,2005. |
| [14] | R. Greenwood;P.F. Luckham;T. Gregory .The effect of particle size on the layer thickness of a stabilising polymer adsorbed onto two different classes of polymer latex, as determined from rheological experiments[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,1995(1/2):117-125. |
| [15] | 李玉涛;汪长安;赵晨辰 .初始浆料中固相含量对莫来石多孔陶瓷显微结构和性能的影响[J].稀有金属材料与工程,2011,40(z1):540-542. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%