测量了再结晶态Ta12W合金板的室温至1 600℃的拉伸性能.在室温下拉伸,Ta12W合金展示出良好的固溶强化和优良的延性.提高试验温度,合金的强度和延性均逐渐下降.特别在800℃时,合金强度急骤下降,其延性达到最低值,加工硬化达到最大,这是由于TaO和TaC固溶产生的动态应变时效所致.在800℃拉伸断口上可以看到局部晶间断裂.在1 000℃至1 600℃拉伸期间,合金强度继续下降,但延性快速升高,在1 000℃拉伸断口上出现由晶界滑动产生的波纹花样形变带.
参考文献
| [1] | Clark J B;Garrett R K;Jungling T L et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,23:2183. |
| [2] | Clark J B;Garrett R K;Jungling T L et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1991,22:2959. |
| [3] | Gypen L A;Deruyttere A .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13:1015. |
| [4] | Mordike B L;Rogausch K D;Braithwaite A A .[J].Journal of Metal Science,1970,4:37. |
| [5] | Gypen L A;Deruyttere A .[J].Journal of the Less-Common Metals,1982,86:219. |
| [6] | 张廷杰;张德尧;丁旭 .[J].稀有金属材料与工程,1996,25(04):6. |
| [7] | 张廷杰,张德尧,丁旭.强冲击载荷下Ta-W合金的塑变特征[J].稀有金属材料与工程,1997(02):12-17. |
| [8] | Pink E;Kumer S;Grill R .[J].International Journal of Refractory Metals and Hard Materials,1997,15:301. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%