以钛酸四丁酯(TRIP)为原料、硝酸铁为掺杂剂、冰醋酸为催化剂、甲酰胺为干燥控制化学添加剂,采用溶胶-凝胶法制备Fe3+掺杂TiO2醇凝胶,并结合常压干燥工艺,实现了Fe3+掺杂TiO2气凝胶的常压干燥法制备.采用XRD、BET、SEM、IR等对样品进行检测.结果表明:制备态Fe3+掺杂TiO2气凝胶密度为0.24 g/cm3,比表面积为529.17 m2/g,平均孔径约为20.10 nm,晶型为无定形；经850℃空气气氛下煅烧2h后,样品转变为锐钛矿型结构,平均孔径增大到22.32 nm,比表面积为136.22 m2/g.通过甲基橙溶液光催化降解实验,相比未掺杂二氧化钛气凝胶,掺入nFe∶nTi=0.05时,样品具有更高的光催化性能.
参考文献
| [1] | Fujishima A;Zhang X T;Tryk D A .Surface Science Reports[J].,2008,63(12):515-582. |
| [2] | Gronauer M;Fficke J .Acoustic Properties of Microporous SiO2-aerogel[J].Acta Acustica,1986,59:177. |
| [3] | Pajonk G M .Aerogel Catalysts[J].Applied Catalysis,1991,72:217. |
| [4] | Lu X;Arduini-Schuster M C;Kuhn J et al.Thermal Conductivity of Monolithic Organic Aerogels[J].Science,1992,255(5047):971. |
| [5] | May S T;Pekala R W;Kaschmitter J L .The Aerocapacitor:an Electrochemical Double-layer Energy-storage Device[J].Journal of the Electrochemical Society,1993,140(02):446. |
| [6] | 王玉栋,甘礼华,郝志显,陈龙武.气凝胶光催化剂的研究进展[J].化工科技,2005(03):36-40. |
| [7] | Choit W;Termin A;HoffmannM R .The Role of Metal Iron Dopants in Quantnm-sised TiO2:Correlation between Photoreactivity and Charge Cartier Recombination Dynamics[J].Journal of Physical Chemistry,1994,98(51):13669-13679. |
| [8] | 张青红,高濂,孙静.氧化硅对二氧化钛纳米晶相变和晶粒生长的抑制作用[J].无机材料学报,2002(03):415-421. |
| [9] | De Bore J H.The Structure and Properties of Porous Materials[M].London:Butterworths,1958:68. |
| [10] | Xu Z J;Gan L H;Jia Y Y et al.Preparation and Characterization of Silica-titania Aerogel-like Balls by Ambient Pressure Drying[J].Sol-Gel Science Technology,2007,41:203-207. |
| [11] | Dutoit DCM.;Baiker A.;Schneider M. .TITANIA-SILICA MIXED OXIDES .1. INFLUENCE OF SOL-GEL AND DRYING CONDITIONS ON STRUCTURAL PROPERTIES[J].Journal of Catalysis,1995(1):165-176. |
| [12] | 张敬畅;高玲玲;曹维良 .纳米TiO2-SiO2复合光催化剂的超临界流体干燥法制备及其光催化性能研究[J].无机化学学报,2005,21(05):638-642. |
| [13] | 胡久刚,陈启元,李洁,卢斌,李鹏举.常压干燥法制备TiO2气凝胶[J].无机材料学报,2009(04):685-689. |
| [14] | 申乾宏,杨辉,高基伟.正硅酸乙酯对锐钛矿型二氧化钛多孔薄膜的室温制备及性能的影响[J].硅酸盐学报,2008(06):788-793. |
| [15] | 甘礼华,张宇星,陈龙武,葛奇.干燥控制化学添加剂在制备硅气凝胶中的应用[J].同济大学学报(自然科学版),2003(09):1131-1134. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%