利用激光熔炼技术制备出Ti5Si3-TiCo-Ti2Co多相金属间化合物新型耐磨合金,分析了合金的显微组织并测试了合金的室温干滑动磨损性能.结果表明,Ti5Si3-TiCo-Ti2Co多相金属间化合物耐磨合金组织均匀、致密,在室温干滑动磨损条件下具有优异的耐磨性能.Ti5Si3-TiCo-Ti2Co多相金属间化合物耐磨合金的磨损量随磨损时间的延长缓慢增加,磨损率先增加后降低;难熔金属硅化物Ti5Si3的高硬度及金属问化合物的反常屈服强度-温度关系及磨损过程中表面粘附转移保护层的形成,是Ti5Si3-TiCo-Ti2Co多相金属间化合物耐磨合金在室温干滑动磨损试验条件下具有较好耐磨性能的原因.
参考文献
| [1] | 孙家枢.金属的磨损[M].北京:冶金工业出版社,1992:1. |
| [2] | 张永刚.金属间化合物结构材料[M].北京:国防工业出版社,2001:1. |
| [3] | Sauthoff G.Intermetallics[M].NY:VCH,1995 |
| [4] | Nakata Y .[J].Materials Science Forum,2000,327-328:449. |
| [5] | Xue Y;Wang HM .Microstructure and wear properties of laser clad TiCo/Ti2CO intermetallic coatings on titanium alloy[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2005(1/4):278-286. |
| [6] | Hofmann H;Frommeyer G;Derder C .[J].Materials Science and Engineering,1998,A245:127. |
| [7] | 洪丽华.[J].武汉大学学报(自然科学版),1998(03):433. |
| [8] | 康朋超.[J].北京科技大学学报,2004(11):187. |
| [9] | Dutta Majumdar J;Mordike B L;Manna L .[J].Wear,2000,242:18. |
| [10] | Dutta Majumdar J;Weisheit A;Mordike B L et al.[J].Materials Science and Engineering,1999,A266:123. |
| [11] | Rao K P;Zhou J B .[J].Materials Science and Engineering,2003,A356:208. |
| [12] | Wang H M;Liu Y F .[J].Materials Science and Engineering,2002,A338:126. |
| [13] | 刘元富,赵海云,王华明.激光熔敷Ti5Si3/NiTi金属间化合物复合材料涂层组织与耐磨性[J].稀有金属材料与工程,2003(05):367-371. |
| [14] | 刘元富,赵海云,王华明.激光熔敷Ti5Si3/NiTi2复合材料涂层的组织与耐磨性[J].材料研究学报,2002(03):313-318. |
| [15] | Wang H M;Luan D Y;Zhang L Y .[J].Scripta Materialia,2003,48:1179. |
| [16] | Villars P;Prince A;Okamoto H.Handbook of Ternary Alloy Phase Diagrams[M].New York:ASM,1995:8676. |
| [17] | Kubaschewski O;Alock C B.Metallurgical Thermochemistry[M].London:Pergamon Press,1979:267. |
| [18] | Nash P.;Schwarz RB.;Choo H. .Thermodynamic calculation of phase equilibria in the Ti-Co and Ni-Sn systems[J].Journal of Materials Science,1998(20):4929-4936. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%