采用体外试验法对纯镁和AZ31B镁合金及阴性对照材料(316L不锈钢)的凝血酶原时间(PT)、血浆复钙时间(RT)动态凝血时间进行了测定,并对这几种材料的血液相容性进行了对比;将纯镁植入大鼠背部肌肉处,研究镁的骨诱导能力.研究结果表明,以PT为指标的抗凝血性能顺序为:Mg＜AZ31B＜316L;以RT和动态凝血时间为指标的抗凝血性能顺序均为:316L＜Mg＜AZ31B;镁有良好的骨诱导性.
参考文献
| [1] | Longchuan Li;Jiacheng Gao;Yong Wang .[J].Surface and Coatings Technology,2004,185:92. |
| [2] | 浦素云.金属植入材料及其腐蚀[M].北京:北京航空航天大学出版社,1990:29. |
| [3] | 邵美珍.镁的基础与临床[M].成都:四川科学技术出版社,1996:3. |
| [4] | Yousef Al-Abdullat;Sadami Tsutsumi;Naoki Nakajima;Makoto Ohta;Hideyuki Kuwahara;Ken Ikeuchi .Surface modification of magnesium by NaHCO{sub}3 and corrosion behavior in hank's solution for new biomaterial applications[J].Materials transactions,2001(8):1777-1780. |
| [5] | Hideyuki Kuwahara;Yousef Al-Abdullat;Naoko Mazaki .Precipitation of Magnesium Apatite on Pure Magnesium Surface during Immersing in Hank's Solution[J].Materials transactions,2001(7):1317-1321. |
| [6] | Wittea F;Kaeseb V;Haferkampb H et al.[J].Biomaterials,2005,26:3557. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%