在传统气体雾化的基础上, 提出了一种新型的气体雾化制粉方法, 即在雾化气流中添加NaCl粉末, 提高气流的冲击动量. 通过对6-6-3青铜, Al, Al-Si, Pb, Sn, Zn等多种材料进行的雾化实验结果表明, 该方法能够有效减小雾化粉末的粒度, 与传统气体雾化相比, 平均粒度可减小50%, 此外还可大幅提高细粉收得率, 且不会过多影响粉末的纯度.
参考文献
| [1] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1997 |
| [2] | Hopkins W G .Fine powder: close-coupled or open-die atomization[J].Metal Powder Report,1990,45(01):41. |
| [3] | Raman R V;Patel A N;Canbonara R S .Rapidly solidified powders produced by a new atomization process[J].Metal Powder Report,1984,39(02):106. |
| [4] | Erich D L;Patel A N .Battelle plan commercialization of two-stage spinning cup atomization process[J].Metal Powder Report,1984,42(10):698. |
| [5] | Anderson I E .Boost in atomizer pressure shaves powder-particle size[J].Current Advances in Materials and Processes,1991,140(01):30. |
| [6] | Anderson I E;Figliola R S;Morton H .Flow mechanisms in high pressure gas atomization[J].Materials Science and Engineering,1991,A148:101. |
| [7] | 陈振华;王云;蒋向阳 et al.快速凝固制粉装置[P].CN:90306130,1990. |
| [8] | 陈振华;王云;蒋向阳.多组快速凝固过程的成粉理论和装置[J].中南矿冶学院学报,1991(z1):11. |
| [9] | 刘允中;陈振华 .多级雾化大过冷及凝固研究[J].中国有色金属学报,1998,8(z1):86. |
| [10] | 陈振华;陈刚;严红革 et al.液体金属与合金的固体雾化方法[P].CN:01106868.x |
| [11] | Alan Lawley.Atomization[M].Metal Powder Industries Federation,PA,1992:105. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%