聚乳酸-羟基乙酸(PLGA)/改性纳米羟基磷灰石(MHA)复合多孔组织工程支架材料的制备主要包含以下步骤:首先通过室温化学共沉淀法制备纳米羟基磷灰石,然后通过L-丙交酯在二甲苯溶液中聚合接枝纳米羟基磷灰石得到改性的纳米羟基磷灰石;最后通过改进的热致相分离两步初化法制备PLGA/MHA复合多孔支架.X射线衍射仪(XRD)显示纳米羟基磷灰石合成成功,透射电子显微镜(TEM)结果显示其为半径为30～50nm的球形,红外光谱显示聚乳酸成功的接枝到纳米羟基磷灰石表面;扫描电子显微镜(SEM)结果表明改进的热致相分离两步初化法制备的PLGA/MHA复合多孔支架的孔径在100～450μm.
参考文献
| [1] | Karageorgiou V;Kaplan D .[J].Biomaterials,2005,26:5454-5491. |
| [2] | Rizzi S C;Heath D J;Coombes A G et al.[J].Journal of Biomedical Materials Research,2001,55:475-486. |
| [3] | Bagambisa F B;Joos U;Schilli W .[J].Journal of Biomedical Materials Research,1993,27(08):1047-1055. |
| [4] | Webster T. J.;Ergun C. .Specific proteins mediate enhanced osteoblast adhesion on nanophase ceramics[J].Journal of biomedical materials research, Part B. Applied biomaterials,2000(3):475-483. |
| [5] | Webster TJ;Siegel RW;Bizios R .Osteoblast adhesion on nanophase ceramics.[J].Biomaterials,1999(13):1221-1227. |
| [6] | Wang M .Developing bioactive composite materials for tissue replacement.[J].Biomaterials,2003(13):2133-2151. |
| [7] | Van L P;Li F;Keustermans J P et al.[J].Journal of Materials Science:Materials in Medicine,1995,6:8-13. |
| [8] | Jagur-Grodzinski J .[J].Polymers For Advanced Technologies,2006,17:395-418. |
| [9] | Zhang Ruiyun;Ma P X .[J].Journal Biomedical Materials Research,1999,44:446-455. |
| [10] | Zhang Ruiyun;Ma P X .[J].Macromolecular Bioscience,2004,4:100-111. |
| [11] | Wei Guobao;Ma P X .[J].BIOMATERIALS,2004,25:4749-4757. |
| [12] | Kim SS;Park MS;Jeon O;Choi CY;Kim BS .Poly(lactide-co-glycolide)/hydroxyapatite composite scaffolds for bone tissue engineering[J].Biomaterials,2006(8):1399-1409. |
| [13] | 王培铭;许乾慰.材料研究方法[M].北京:科学出版社,2005:77-120,127-182,261-303. |
| [14] | 邓芹英;刘岚;邓慧敏.波谱分析教程[M].北京:科学出版社,2003:44-69. |
| [15] | 朱晏军,沈春华,戴红莲,万涛,闫玉华.生物医用纳米羟基磷灰石（HA）的制备及性能测试[J].佛山陶瓷,2004(01):13-15. |
| [16] | 宋云京,李木森,温树林,宿庆才,姜庆辉.浓度、温度和陈化对羟基磷灰石合成的影响[J].机械工程材料,2003(05):19-21. |
| [17] | 江捍平.纳米羟基磷灰石的研究进展[J].中国医学工程,2004(06):32-35. |
| [18] | 宋云京,李木森,温树林,姜庆辉,宿庆财.温度和pH值对羟基磷灰石粉体合成的影响[J].硅酸盐通报,2003(02):7-10. |
| [19] | Feng J H;Tae G P;Doo S L.[J].POLYMER,2003(44):1911-1920. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%