Crystallization kinetics of Fe55-xCrzsMo7B10C4Nbx（x= 0, 3） bulk amorphous alloys were analyzed using X-ray diffraction and differential scanning; calorimetric （DSC） tests. In practice, crystallization and growth mechanism were evaluated using DSC tests at four different heating rates （10, 20, 30, and 40 K/rain） and kinetic models. Two-step crystallization behavior was observed when Fe55Cr18MOTB16C4 and Fe52Cr18MoTB16C4Nb3 bulk amorphous alloys were annealed, where Fe36Cr12M010 phase was crystallized in the first step of crystallization. Results show that Fe36Cr12Mo10 and Fe3C phases were crystallized in the structures of the alloys after further annealing： process. Activation energy for the crystallization of Fe36Cr12Mozo phase was measured to be 543 kJ/mol in Fe52Cr18MoTB16C4Nb3 alloy and 375 kJ/mol for Fe55Cr18Mo7B16C4 alloy according to Kissinger-Starink model. Moreover, a two-dimensiona nucleation rate was found in Fe52Cr18Mo7B16C4Nb3 diffusion controlled growth mechanism with decreasing alloy whereas a three-dimensional diffusion controlled growth mechanism with decreasing nucleation rate was found in crystallization of Fe36Crz2Mo10 phase during annealing of Fe55Cr18MoTB16C4 alloy. TEM （transmission electron microscopy） observations reveal that crystalline Fe36Cr12M010 phase nucleated in the structures of the alloys in an average size of 10 nm with completely mottled morphology.
参考文献
| [1] | W.H. Wang;C. Dong;C.H. Shek .Bulk metallic glasses[J].Materials Science & Engineering, R. Reports: A Review Journal,2004(2/3):45-89. |
| [2] | R.M. Ribeiro;D.S. dos Santos;R.S. de Biasi .Crystallization kinetics of the (Fe_(50)Co_(50))_(73.5)Ag_1Nb_3Si_(13.5)B_9 amorphous alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2004(1/2):227-230. |
| [3] | D.M. Minic;A. Maricic;B. Adnadevic .Crystallization of a-Fe phase in amorphous Fe_(81)B_(13)Si_4C_2 alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):363-367. |
| [4] | D.J. Branagan;M.C. Marshall;B.E. Meacham .High toughness high hardness iron based PTAW weld materials[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):116-123. |
| [5] | D.J. BRANAGAN;W.D. SWANK;D.C. HAGGARD .Wear-Resistant Amorphous and Nanocomposite Steel Coatings[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2001(10):2615-2621. |
| [6] | S. Ahmadi;H. Arabi;A. Shokuhfar .Formation mechanisms of precipitates in an Al-Cu-Li-Zr alloy and their effects on strength and electrical resistance of the alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):90-94. |
| [7] | I.C. Rho;C.S. Yoon;C.K. Kim .Crystallization of amorphous alloy Co_(68)Fe_4Cr_4Si_(13)B_(11)[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2002(1):48-52. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%