以某钢厂圆坯连铸机为研究对象,建立了连铸坯凝固传热模型。在不同拉速下对280 mm断面圆坯二次冷却过程进行仿真优化,确定了16MnNb钢合适的二冷制度。根据仿真结果,在最小工作拉速(0.9 m/min)下,矫直点处铸坯内弧表面中心温度为947℃,有效避开了铸坯的二次低延性区。在最大工作拉速(1.2 m/min)下,铸坯出结晶器时,其凝固坯壳厚度为19 mm,二冷初期产生漏钢等质量问题的可能性较小。不同拉速下,横断面温度场分布均匀。经低倍检测发现,铸坯表面及内部质量良好,无裂纹、疏松、缩孔等质量缺陷。
The heat transfer model for solidification of continuous casting billet has been established, based on a round caster in a steel plant. The simulation and optimization were carried out at different drawing speeds when continuous cast-ing billet with diameter of 280 mm was in secondary cooling process. Suitable secondary cooling scheme of 16MnNb steel was determined. When the drawing speed is the minimum of 0.9 m/min, the inner arc surface temperature of billet is 947℃at straightening point, which can effectively avoid the secondary low ductile zone. When the round billet comes out of mould at the maximum drawing speed (1.2 m/min), the thickness of the solidified shell is 19 mm. Some problems such as breakout hardly happen. The section temperature is uniformly distributed under different drawing speed conditions. The macro inspecting indicates that the round billet surface and internal quality are good. Crack and contraction cavities and other defects were not found.
参考文献
[1] | 孙维,汪开忠.Nb微合金化钢异型坯连铸二冷工艺参数的确定[J].连铸,2001(05):4-5,23. |
[2] | Turkdogan E .Causes and Effects of Nitride and Carbonitride Precipitation During Continuous Casting[J].Iron Steelmaker,1989,16(05):61. |
[3] | Maehara Y;Yasumoto K;Tomono H et al.Surface Cracking Mechanism of Continuously Cast Low Carbon Low Alloy Steel Slabs[J].Materials Science and Technology,1990,6(09):793. |
[4] | Michel Bellet;Alban Heinrich .A Two-Dimensional Finite Ele-ment Thermomechanical to a Global Stress-Strain Analysis of Steel Continuous Casting[J].ISIJ International,2004,44(10):186. |
[5] | Janik M;Dyja H;Berski S .Two-Dimensional Thermome-Chani-cal Analysis of Continuous Casting Process[J].Materials Pro-cessing Technology,2004,153(11):578. |
[6] | 黎建全,陈登福,吴国荣,雷阳伟.37Mn2钢连铸圆坯的二次冷却制度[J].钢铁,2014(01):45-51. |
[7] | 潘贻芳,祭程,张晓博,蔡兆镇,罗森,朱苗勇.宽厚板坯连铸二冷工艺开发与应用[J].中国冶金,2012(09):42-46,50. |
[8] | 凌钢2号方坯连铸机二冷制度的优化[J].中国冶金,2005(10):34-36. |
[9] | 王水根 .圆坯连铸凝固传热模型及二冷动态控制研究[D].重庆大学,2010. |
[10] | 陈登福,孙明月,冯科,赵战锋,董凌燕,温良英,潘艳华.方坯连铸二次冷却数值仿真商用软件[J].重庆大学学报(自然科学版),2004(09):67-71. |
[11] | 龙木军,陈登福,靳星.板坯连铸通用仿真模型算法的研究及软件开发[C].第四届发展中国家连铸国际会议论文集,2008:548-551. |
[12] | Qing Liu,Liangzhou Wang,Liqiang Zhang,Liguo Cao,Xiuzhong Ding,Mei Liang,Yongge Qi.Mathematical model of heat transfer for bloom continuous casting[J].北京科技大学学报(英文版),2008(01):17-23. |
[13] | 蔡开科.连续铸钢原理与工艺[M].北京:冶金工业出版社,1994 |
[14] | 杨吉春;蔡开科 .连铸二冷区喷雾冷却特性研究[J].钢铁,1990,25(02):9. |
[15] | Teshima Toshio;Kitagawa Toru;Miyahara Shinobu et al.The Secondary Cooling Technology of Continuous Casting for Pro-duction of High Temperature and High Quality Slab[J].ISIJ In-ternational,1988,74(07):1282. |
[16] | RICHARD A. HARDIN;KAI LIU;ATUL KAPOOR .A Transient Simulation and Dynamic Spray Cooling Control Model for Continuous Steel Casting[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2003(3):297-306. |
[17] | 文光华;迟景颢;黄云飞 .连铸机二冷喷嘴冷态和热态的试验研究[J].钢铁研究,1997,98(05):24. |
[18] | 王水根;陈登福.圆坯连铸二次冷却计算机通用仿真软件的开发[A].深圳:中国金属学会炼钢分会,2010 |
[19] | 李延生.连铸坯缺陷的成因及防止对策[J].炼钢,1998(03):55. |
[20] | Mintz B;Mohamed Z;Abu-Shosha R .Influence of Calcium on Hot Ductility of Steels[J].Materials Science and Technology,1989,5(07):682. |
[21] | Mintz B;Yue S;Jonas J .Hot Ductility of Steels and its Relation-ship to the Problem of Transverse Cracking During Continuous Casting[J].International Materials Reviews,1991,36(01):187. |
[22] | 傅广瑞;郑贤淑;金俊泽 .碳素钢连铸坯高温力学性能的研究[J].钢铁研究学报,1993,5(03):15. |