为解决目前四羟丙基乙二胺(THPED)-EDTA "2Na盐化学镀铜体系存在的镀速慢、稳定性不佳等问题,重点考察了不同添加剂对THPED-EDTA·2Na盐化学镀铜的影响.结果表明:硫脲(＞3 mg/L)、2-巯基苯并噻唑(2-MBT)和有机物M(含巯基的咪唑类化合物)对镀液的稳定效果较好;硫脲会极大地降低沉积速率,且镀层较差;2-MBT可以提高沉积速率,但稳定镀液的能力有限;有机物M兼有加速剂、稳定剂和光亮剂的功能,对镀液的稳定效果最好,且镀层光亮细致;吐温-80和亚铁氰化钾均能改善镀层外观质量,但对沉积速率及镀液稳定性的影响不大;通过正交试验,以有机物M与2-MBT,吐温-80和亚铁氰化钾复配,确定了最优复合添加剂配方:2-MBT 7mg/L,有机物M 20 mg/L,亚铁氰化钾10 mg/L,吐温-80 20 mg/L;在适宜工艺条件(温度40℃,pH值12.5)下,镀速达到16.3 μm/h,镀液稳定时间可达146 min,所得镀层平整、光亮、细致,沉积层为立方晶系铜,PCB孔覆背光级数达到9级,满足PCB工业生产要求.
参考文献
| [1] | 杨防祖,吴丽琼,黄令,郑雪清,周绍民.以次磷酸钠为还原剂的化学镀铜[J].电镀与精饰,2004(04):7-9,24. |
| [2] | S. Karthikeyan;T. Vasudevan;K. N. Srinivasan;S. John .Studies on formaldehyde-free electroless copper deposition[J].Plating & Surface Finishing,2002(7):54-56. |
| [3] | Ando;Setsuo E;Minoru N et al.Electrolytic copper plated R-T-B magnet and plating method thereof[P].US,6866765,2002-01-17. |
| [4] | Donahue F M;Sajkowski D J;Bosio A C .Kinetics of electroless copper plating inhibition by adsorption of ligand[J].Journal of the Electrochemical Society,1982,129(40):717-719. |
| [5] | 廖小波.一种性能优异的化学镀铜溶液体系[J].新兴科技,1992(3):11-16. |
| [6] | 郑雅杰,邹伟红,易丹青,龚竹青,李新海.四羟丙基乙二胺和EDTA·2Na盐化学镀铜体系研究[J].材料保护,2006(02):20-24. |
| [7] | 申晓妮,赵冬梅,任凤章,田保红.添加剂对四羟丙基乙二胺（THPED）化学镀厚铜的影响[J].中国腐蚀与防护学报,2011(05):362-366. |
| [8] | 孔德龙,谢金平,范小玲,肖宁,黎德育,李宁.化学镀铜溶液中稳定剂的研究[J].电镀与精饰,2014(03):5-9. |
| [9] | 邹伟红 .快速化学镀铜工艺及机理研究[D].中南大学,2005. |
| [10] | Li J;Hayden H;Kohl P A .The influence of 2,2 primedipyridyl on non-formaldehyde electroless copper plating[J].Electrochimica Acta,2004,49(11):1785-1795. |
| [11] | Oita M;Matsuoka M;Iwakura C .Deposition rate and morphology of electroless copper film from solutions containing 2,2'-dipyridyl[J].Electrochimica Acta,1997,42(9):1435-1440. |
| [12] | 朱焱,孔小雁,江茜,王未燕.表面活性剂在陶瓷化学镀铜工艺中的作用[J].中国表面工程,2012(01):76-82. |
| [13] | L. L. Duda .Effect of isomeric dipyridyls on electroless copper deposition from EDTA solutions[J].Plating & Surface Finishing,1998(7):60-62. |
| [14] | Farid Hanna;Z. Abdel Hamid;A. Abdel Aal .Controlling factors affecting the stability and rate of electroless copper plating[J].Materials Letters,2004(1/2):104-109. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%