采用极化曲线法和循环伏安法研究了K4P2O7·3H2O+Sn2P2O7溶液体系中Sn (Ⅱ)的阴极还原反应机理和动力学规律.结果表明,焦磷酸盐溶液体系电沉积Sn的表观活化能为13～14 kJ/mol,即电极过程遵循扩散控制的动力学规律.Sn2+在焦磷酸盐溶液中的主要存在形式是[Sn(P2O7)2]6-,但在阴极直接放电还原的是[Sn(P2O7)]2-,电沉积锡的可能机理为:[Sn(P2O7)2]6(=)[Sn(P2O7)]2-+ P2O74-;[Sn(P2O7)]2-+ 2e-→Sn+ P2O74-.
参考文献
| [1] | VAID J;RAMA CHAR T L .Tin plating from the pyrophosphate bath[J].Journal of the Electrochemical Society,1957,104(05):282-287. |
| [2] | TAMURA N;OHSHITA R;FUJIMOTO M et al.Study on the anode behavior of Sn and Sn-Cu alloy thin-film electrodes[J].Journal of Power Sources,2002,107(01):48-55. |
| [3] | Chunfen Han;Qi Liu;Douglas G. Ivey .Nucleation of Sn and Sn-Cu alloys on Pt during electrodeposition from Sn-citrate and Sn-Cu-citrate solutions[J].Electrochimica Acta,2009(12):3419-3427. |
| [4] | Hsieh, JC;Hu, CC;Lee, TC .Effects of polyamines on the deposition behavior and morphology of zinc electroplated at high-current densities in alkaline cyanide-free baths[J].Surface & Coatings Technology,2009(20/21):3111-3115. |
| [5] | 郭艳,曾振欧,赵洋,谢金平,李树泉.焦磷酸盐溶液体系电沉积白铜锡的电化学行为[J].电镀与涂饰,2014(08):317-320. |
| [6] | 黄灵飞,曾振欧,冯冰,谢金平,李树泉.焦磷酸盐溶液体系电沉积铜及铜-锡合金的电化学行为[J].电镀与涂饰,2014(07):275-278. |
| [7] | 张锦秋 .锡银铜合金的电沉积工艺与沉积机制及其焊接性能的研究[D].哈尔滨工业大学,2009. |
| [8] | 吴伟刚,杨防祖,姚士冰,陈秉彝,郑雪清,周绍民.柠檬酸盐碱性镀铜的电化学行为研究[C].2009年全国电子电镀及表面处理学术交流会论文集,2009:88-92. |
| [9] | 许利剑,杜晶晶,汤建新,张继德.电沉积Ni-Cr合金电化学行为的研究[J].材料保护,2008(02):23-25. |
| [10] | BERZINS T;DELAHAY P .Oscillographic polarographic waves for the reversible deposition of metals on solid electrodes[J].Journal of the American Chemical Society,1953,75(03):555-559. |
| [11] | 曹鹏 .多元共电沉积Mg-Li-X(X=Sn,La,Zn-Mn)合金及机理研究[D].哈尔滨工程大学,2012. |
| [12] | 左正忠;何细华;侯润香 .无氰溶液中电沉积铜锡合金电化学行为的研究[J].武汉大学学报(自然科学版),1996,42(02):141-145,166. |
| [13] | 冯冰 .焦磷酸盐溶液体系滚镀低锡铜-锡合金(黄青铜)工艺及电沉积动力学[D].广州:华南理工大学,2013. |
| [14] | 程骄 .PCB上镀锡工艺研究及其电化学过程探讨[D].湖北工业大学,2010. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%