采用搅拌熔铸法制备双粒径SiCp/Al复合材料，利用扫描电镜（SEM）、电子万能试验机研究搅拌温度对复合材料的微观结构以及力学特性的影响。结果表明：SiC含量随着搅拌温度的升高而增加，在585℃两种粒径混合的SiC颗粒弥散分布在基体上，随温度继续升高，基体出现明显的贫SiC区域；复合材料的抗压强度、抗弯强度以及最大弯曲挠度均随着搅拌温度的升高先增大后减小，在585℃达到最大值，力学特性较纯铝、单一粒径的SiCp/ZL107复合材料有明显提高。SiC颗粒的分布以及界面结合强度决定复合材料的断裂机制。
SiCp/ZL107 composites with two particle sizes were prepared by stirring casting. The influence of stirring temperature on microstructure and mechanical properties of the composites was investigated by scanning electron microscopy(SEM),energy dispersive spectroscopy(EDS)and electronic universal testing machine. The results show that the content of SiC increases with the increase of stirring temperature,and the SiC particles with two particle sizes are diffusely distributed on the substrate when the stirring temperature is 585℃. There is an obvious poor SiC region with the continuous increase of stirring temperature. The compressive strength,flexural strength,and maximum deflection of composites along with the stirring temperature increases first and then decreases,reaches its maximum at 585 ℃. Compared with the pure aluminum and single particle size SiCp/ZL107 composites,the mechanical properties of two particle sizes SiCp/ZL107 composites increase significantly. The failure mechanism of the composites is determined by the distribution of SiC and the interfacial bonding strength.
参考文献
| [1] | 南宏强,袁森,王武孝,张菊梅,王志虎,罗红斌.工艺因素对SiCp/AZ91复合材料颗粒均匀性的影响[J].特种铸造及有色合金,2007(04):302-305. |
| [2] | Tamer Ozben;Erol Kilickap;Orhan Cakir .Investigation of mechanical and machinability properties of SiC particle reinforced Al-MMC[J].Journal of Materials Processing Technology,2008(1-3):220-225. |
| [3] | 王海龙,汪长安,张锐,黄勇,许红亮,卢红霞.纳米SiC晶须和SiC颗粒混合增韧ZrB2陶瓷性能[J].复合材料学报,2009(04):95-101. |
| [4] | 刘有金,张云龙,高晶,胡明.SiC颗粒尺寸对SiCp/Cu基复合材料热膨胀系数的影响[J].兵器材料科学与工程,2013(01):118-121. |
| [5] | 苏海,高文理,毛成,刘洪波,卢健,陆政.搅拌铸造SiCp/2024复合材料的研究[J].湖南大学学报（自然科学版）,2009(08):54-58. |
| [6] | Grigoris E K;Stefanos M S;George A L .Aging response of alu-minum alloy 2024/silicon carbide particles(SiCp)composites[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,382(1/2):351-361. |
| [7] | 袁武华,张健,陈振华,刘斌.超高强7090/SiCP复合材料的组织和性能[J].机械工程材料,2006(09):39-43. |
| [8] | 李进,周春玲,杨智春.SiCp/Al功能梯度复合材料的压缩性能研究[J].兵器材料科学与工程,2009(03):33-36. |
| [9] | Kaynak C;Boylu S .Effect of SiC particulates on the fatigue be-havior of an Al-alloy matrix composite[J].Materials and De-sign,2006,27(09):776-782. |
| [10] | 袁武华,安佰玲.热处理对挤压态7090/SiCp复合材料组织和力学性能的影响[J].中国有色金属学报（英文版）,2012(09):2080-2086. |
| [11] | 陈振华,贺毅强,陈志钢,尹显觉,陈刚.SiCp/Al-8.5Fe-1.3V-1.7Si复合材料的显微组织及室温力学性能[J].中国有色金属学报,2007(06):858-864. |
| [12] | 王鹏,马乃恒,李险峰,王浩伟.原位合成铝基复合材料中颗粒沉降的研究[J].特种铸造及有色合金,2004(02):30-32. |
| [13] | 赵龙志,曹小明,田冲,胡宛平,邢宏伟,张劲松.浇注温度对SiC泡沫/SiCp/Al混合复合材料力学性能的影响[J].金属学报,2006(01):103-108. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%