以NiCr-Cr3C2混合粉末为原料,对γ-TiAl金属间化合物合金进行激光表面合金化,制得了以γ-NiCrAl镍基固溶体为基体、以TiC及Cr7C3为增强相的复合材料表面改性层,分析了激光表面合金化改性层的组织,并测试了其在滑动磨损试验条件下的耐磨及高温抗氧化性能.试验结果表明,上述激光表面合金化层具有很高的硬度、较高的耐磨性及高温抗氧化性.
参考文献
| [1] | 山口正治;丁树深译.Intermetallics[M].北京:科学出版社,1991 |
| [2] | Dimiduk D M .Materials Science and Engineering[J].,1999,A263:281-288. |
| [3] | Xu D et al.[J].Surface and Coatings Technology,1994,66:486-494. |
| [4] | Laniguchi S et al.[J].ISJ International,1993,33:869-876. |
| [5] | Gredic I et al.[J].Surface and Coatings Technology,1993,61:338-345. |
| [6] | Huang B et al.[J].Transactions of Nonferrous Metal Society of Clhina,1994,4:59-61. |
| [7] | 张永刚.[J].Surface and Coatings Technology,1998(100-101):214-218. |
| [8] | Yoshihara M et al.[J].ISJ International,1991,31:1201-1206. |
| [9] | Wang Y et al.[J].Surface and Coatings Technology,1997,91:37-42. |
| [10] | Noda T et al.[J].Materials Science and Engineering,1996,A213:157-161. |
| [11] | 王华明 .第一届亚洲摩擦学会议[M].北京:清华大学出版社,1998,2:603-607. |
| [12] | 王华明 et al.[J].金属学报,1997,33(08):917-920. |
| [13] | 何秀丽 et al.[J].金属学报,1998,34(09):983-986. |
| [14] | 王华明.TiAl金属间化合物合金的激光气体合金化表面改性研究[J].中国激光,1997(11):1049. |
| [15] | 表面工程手册[S].北京:化学工业出版社,1998. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%