采用密度泛函平面波超软赝势方法,系统研究了Nd掺杂前后金红石相TiO2的电子结构变化,计算结果表明:Nd掺杂使TiO2的电子态发生重新分布,分能带明显增加;在导带的下方出现了一些新的电子态,分波态密度的结果进一步证实,这些新的态归属于Nd 4d轨道;金红石TiO2的带隙引Nd 4f态的引入而明显降低,并导致材料的带隙减小;Nd掺杂前后金红石相TiO2的紫外-可见漫反射光谱的测试结果表明Nd掺杂TiO2的紫外可见吸收光谱发生红移.
参考文献
| [1] | Augugliaro, V.;Bellardita, M.;Loddo, V.;Palmisano, G.;Palmisano, L.;Yurdakal, S. .Overview on oxidation mechanisms of organic compounds by TiO _2 in heterogeneous photocatalysis (Review)[J].Journal of photochemistry and photobiology, C. Photochemistry reviews,2012(3):224-245. |
| [2] | 李志祥,许高杰,李勇,王琴,孙爱华,段雷,李亚丽,蒋俊.SnO2掺杂对TiO2压敏电阻器性能的影响[J].稀有金属材料与工程,2007(z2):177-180. |
| [3] | 杨少凤,罗薇,朱燕超,刘艳华,赵敬哲,王子忱,邹广田.单一板钛矿相TiO2微晶的制备[J].高等学校化学学报,2003(11):1933-1936. |
| [4] | 王传义,刘春艳,沈涛.半导体光催化剂的表面修饰[J].高等学校化学学报,1998(12):2013-2019. |
| [5] | Palomares E.;Clifford JN.;Haque SA.;Lutz T.;Durrant JR. .Control of charge recombination dynamics in dye sensitized solar cells by the use of conformally deposited metal oxide blocking layers[J].Journal of the American Chemical Society,2003(2):475-482. |
| [6] | 时百成,刘涌,宋晨路,韩高荣.第一性原理方法研究硫掺杂二氧化钛的能带结构[J].稀有金属材料与工程,2008(z2):638-640. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%