A kind of novel compound containing S and Mo elements was synthesized. Its chemical structure was characterized by elemental analysis, IR and NMR. Its anti-wear property and the load-carrying capacity, as an extreme pressure (EP) additive of lubricating oil, were investigated using a four-ball tester. The experimental results show that the additive exhibits a superior anti-wear property and a high load-carrying capacity .The presence of other additives does not interfere with the anti-wear property of the extreme pressure additive. The influences of load and temperature on the property of the additive were examined. The possible mechanism was investigated by means of surface analysis of the tested steel ball specimen, using XPS. The lubrication films formed on the rubbing surface are mainly composed of MoS2,MoO3 and MoO2.
参考文献
| [1] | Robert F B .Molybdenum IV Compounds Process for Preparation and Lubricant Compositions Containing Same[P].US 4428861,1984-07-31. |
| [2] | 文庆珍,朱金华,姚树人,张宝真.烃基的结构对有机钼化合物极压抗磨性能的影响[J].润滑与密封,2000(06):21-23. |
| [3] | 文庆珍,朱金华,姚树人,张宝真.影响硫磷钼化合物极压抗磨性能的因素[J].润滑与密封,2003(02):43-44. |
| [4] | 谢凤,胡建强,姚俊兵,刘广龙.有机钼化合物在成品油中的抗磨性能研究[J].润滑与密封,2004(06):86-88. |
| [5] | 朱金华,文庆珍,张宝真,姚树人.含S、Mo有机化合物的减摩抗磨性能的研究[J].润滑与密封,1999(06):14-15. |
| [6] | Isoyama H;Sakurai T .The Lubricating Mechanism of Dithio-bis (diethyldithio carbamate) Molybdenum During EP Lubrication[J].Trtbol Int,1994,7(04):151-160. |
| [7] | 史佩京,徐滨士,马世宁,乔玉林,刘维民,夏延秋.油溶性有机钼添加剂的摩擦学性能及其摩擦化学作用机制[J].摩擦学学报,2004(02):128-133. |
| [8] | Black A L;Dunster R W;Sanders J V .Comparative Study of Surface Deposits and Behaviour of Mas,Particles and Molybdenum Dialkyl-dithio-phosphate[J].WEAR,1999,13(02):119-132. |
| [9] | Michell P C .Oil-soluble Mo-S Compounds as Lubricant Additives[J].WEAR,1984,100:281-300. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%