采用三元微观相场动力学模型,模拟研究了973,1173,1253 K时效温度下,Ni75Al15Fe10合金中γ'相的早期沉淀过程.通过对该合金原子显微形貌,长程序参数和浓度及Fe原子在不同格点占位分数随时间演化的模拟计算分析得出:随着温度的升高,Ni75Al15Fe10合金的沉淀机制由等成分有序化兼失稳分解机制向非经典形核长大机制过渡;γ'相沉淀析出的孕育期变长;Fe原子在B格点的占位越来越困难,占位几率降低;合金沉淀析出的γ'相为单一L12结构的Ni3(AlFe)复合相.
参考文献
| [1] | Cermak J;Rothova V .[J].Acta Materialia,2003,51(15):4411. |
| [2] | 褚忠,陈铮,王永欣,卢艳丽,李永胜.Ni-Cr-Al合金有序化早期原子尺度的模拟[J].稀有金属材料与工程,2006(02):242-246. |
| [3] | Kozubski R;Soltysi J;Cadevillet M C .[J].J Phys:Condens,1990,2(15):3451. |
| [4] | Himuro Y;Tanaka Y;Kamiya N et al.[J].Intermetallics,2004,12(06):635. |
| [5] | Partyka E;Kozubski R .[J].Intermetallics,2004,12(02):213. |
| [6] | Lechermann F;F(a)hnle M;Sanchez J M .[J].Intermetallics,2005,13(10):1096. |
| [7] | Khachatuyran A G.Theory of Structural Transformations in Solids[M].New York:Wiley Press,1983 |
| [8] | Poduri R;Chen L Q .[J].Acta Materialia,1998,46(05):1719. |
| [9] | Poduri R;Chen L Q .[J].Acta Materialia,1998,46(11):3915. |
| [10] | Almazouzi A;Numakura H;Koiwa M et al.[J].Intermetallics,1997,5(01):37. |
| [11] | Pascarelli S;Boscherini F;Lawniczak-Jablonska K et al.[J].Physical Review B,1994,49(21):14984. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%