研究了CCF300碳纤维/5405双马树脂复合材料在71℃恒温水浸循环吸湿-脱湿行为。试样经过三次饱和吸湿-脱湿过程,探讨不同循环次数CCF300/5405复合材料的吸湿率和水分扩散速率变化,并采用SEM观察纤维/基体界面变化,分析了造成循环湿热环境下复合材料体系吸湿-脱湿变化的原因。研究结果表明：CCF300/5405复合材料的吸湿行为基本满足Fick第二定律,并且在水浸14天后达到饱和吸湿状态,饱和吸湿率约为0.66%;材料吸湿处理后,纤维与基体间的界面遭到水分破坏,产生大量空隙和裂纹,使水分的扩散速率明显增加,饱和吸湿率略有增大,并且这种破坏不可逆。
The cyclic moisture absorption and desorption behavior of CCF300 carbon fiber/5405 bismaleimid composites immersed in 71 ℃ distilled water were investigated.After three cycles of moisture absorption-desorption process,moisture diffusion coefficient and moisture uptake of CCF300/5405 composites in different cycles were studied.Using SEM,the change mechanism of absorption behavior of composites in the hygrothermal condition was discussed.The results show that the moisture absorption behavior of CCF300/5405 composites basically conforms the Fick＇s second law.After 14 days of moisture absorption,the composites reach to the saturated moisture level,and saturated moisture uptake is about 0.66%.Additionally,after cycles of moisture absorption process,the interface between fiber and matrix is damaged by moisture,which leads to a large number of voids and cracks.As a result,water diffusion coefficient increases significantly and saturated moisture uptake rises slightly.Furthermore,the damage is irreversible even after the moisture desorpion.
参考文献
| [1] | Wan Y Z, Wang Y L, Huang Y, He B M, Han K Y. Hygrothermal aging behaviour of VARTMed three-dimensional braided carbon-epoxy composites under external stresses [J]. Composites Part A: Applied Science and Manufacturing, 2005, 36(8): 1102-1109. |
| [2] | Biro D A, Pleizer G, Deslandes Y. Application of the microbond technique: Effects of hygrothermal exposure on carbon-fiber/epoxy interfaces [J]. Composites Science and Technology, 1993, 46(3): 293-301. |
| [3] | 赵稼祥.世界碳纤维现状与进展[J]. 玻璃钢/复合材料, 2003(2): 40-43. |
| [4] | 王茂章, 贺福. 碳纤维的制造、性质及其应用[M]. 北京: 科学出版社, 1984: 1-2. |
| [5] | Zhou J, Lucas J P. The effects of a water environment on anomalous absorption behavior in graphite/epoxy composites [J]. Composites Science and Technology, 1995, 53(1): 57-64. |
| [6] | 彭雷, 张建宇, 鲍蕊. 湿热、紫外环境对T300/QY8911复合材料孔板静力性能的影响[J]. 复合材料学报, 2009, 26(3): 18-23. |
| [7] | Theocaris P S, Papanicolaou G C, Kontou E A. Interrelation between moisture absorption, mechanical behavior and extent of the boundary interphase in particulate composites [J]. Journal of Applied Polymer Science, 1983, 28(10): 3145-3153. |
| [8] | Akbar Sohaib, Zhang Tao, et al. Moisture diffusion in carbon/epoxy composite and the effect of cyclic hygrothermal fluctuations: Characterization by dynamic mechanical analysis (DMA) and interlaminar shear strength (ILSS) [J]. Adhesion, 2008, 84(7): 590. |
| [9] | 过梅丽, 肇研. 航空航天结构复合材料湿热老化机理的研究 [J]. 宇航材料工艺, 2002(4): 51-54. |
| [10] | Bonniau P, Bunsell A R. A comparative study of water absorption theories applied to glass epoxy composites[J]. Composite Materials, 1981, 15(3): 272-293. |
| [11] | Jacobs P M, Jones E R. Diffusion of moisture into two-phase polymers, PartⅡ: Styrenated polyester resins [J]. Journal of Materials Science, 1989, 24(7): 2343-2347. |
| [12] | Selzer R, Friedrich K. Mechanical properties and failure behaviour of carbon fibre-reinforced polymer composites under the influence of moisture [J]. Composites A, 1997, 28(6): 595-604. |
| [13] | George S C, Thomas S. Transport phenomena through polymeric systems [J]. Progress in Polymer Science, 2001, 26(6): 985-1017. |
| [14] | Apicella A, Nicolais L. Hygrothermal history dependence of equilibrium moisture sorption in epoxy resins [J]. Polymer, 1981, 22(8): 1064-1067. |
| [15] | Sarti G C, Apicella A. Non-equilibrium glassy properties and their relevance in Case Ⅱ transport kinetics [J]. Polymer, 1980, 21(9): 1031-1036. |
| [16] | Wong T C, Broutman L J. Moisture diffusion in eposy resins Part Ⅰ : Non-Fickian sorption processes [J]. Polymer Engineering and Science, 1985, 25(9): 521-528. |
| [17] | Jedidi J, Jacquemin F, Vautrin A, et al. Design of accelerated hygrothermal cycles on polymer matrix composites in the case of a supersonic aircraft [J]. Composites Structure, 2005, 68(4): 429-437. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%