针对低碳铝镇静钢连续热镀锌板抗时效性能较差的问题,通过镀锌板时效指数测量和内耗测量研究了卷取温度对抗时效性能的影响.试验结果表明,在620～710℃,随热轧卷取温度的提高,镀锌板固溶碳含量降低,抗时效性能提高,卷取温度从620℃提高到710℃,镀锌板时效指数降低19％.适当提高热轧卷取温度是改善低碳铝镇静钢热镀锌板抗时效性能的有效手段之一.
参考文献
| [1] | 李九龄.带钢连续热镀锌[M].北京:冶金工业出版社,2010 |
| [2] | 程国平,王利.平整对罩式退火生产BH钢板力学性能和自然时效性能的影响[J].钢铁,2003(09):43-45,66. |
| [3] | Riccardo RIVA;Carlo MAPELLI;Roberto VENTURING .Effect of Coiling Temperature on Formability and Mechanical Properties of Mild Low Carbon and HSLA Steels Processed by Thin Slab Casting and Direct Rolling[J].ISIJ International,2007(8):1204-1213. |
| [4] | 王岩,赵爱民,陈银莉,左碧强,薛俊平.不同卷取温度低碳钢性能及硫化物析出的研究[J].钢铁,2011(01):60-65. |
| [5] | Telmo Oliveira de Souza;Vicente Tadeu Lopes Buono .Optimization of the strain aging resistance in aluminum killed steels produced by continuous annealing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):212-216. |
| [6] | 王润.金属材料物理性能[M].北京:冶金工业出版社,1992 |
| [7] | 王玉,刘炜丽,曹晓晖,王守晶.轧制工艺对MR T-2.5镀锡基板C原子固溶的影响[J].沈阳理工大学学报,2010(04):55-58,4. |
| [8] | 沈中城,张进峰,严勇健,关大友.精密扭摆内耗仪的研究进展及其钢中固溶碳测定[J].上海交通大学学报,2010(05):683-686. |
| [9] | S.K.Chang .Effect of Manganese on Aging in Low Carbon Sheet Steels[J].ISIJ International,1997(1):74-79. |
| [10] | Brian PickeringF;刘嘉禾.钢的组织与性能[M].北京:科学出版社,1999 |
| [11] | 带钢连续热镀锌及其退火炉的技术进步[J].国外金属热处理,2005(05):1-4,14. |
| [12] | 杨浩;王浩;赵骧 .退火和平整工艺对镀锡板固溶碳含量的影响[J].中国材料科学与设备,2011,7(03):68. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%