Direct diffusion bonding of an orthorhombic Ti2AINb base alloy to a TiAl base alloy, Ti-22Al-23Nb-2Ta and Ti-46.2Al-2Cr-2Nb-0.15B (at. pet), was carried out and the interface microstructure, formation of new phase at the interface and joint strength were characterized. At low temperature, a new phase with AlNb2-structure, Al(Nb, Ti)_2, was formed in the interface region adjacent to the 0 base alloy. Theα2 was found to be the major reaction product and developed in the interface region adjacent to the TiAl alloy as well as in the region adjacent to the 0 base alloy accompanying the formation of Al(Nb, Ti)_2. The occurrence of AI(Nb, Ti)_2 has been attributed to the different diffusivity of Nb and Al, leading to a eutectoid-like reaction. At relatively high temperature, Al(Nb, Ti)_2 did not form due to enhanced diffusion of Nb but a B2-enriched zone formed on the 0 alloy side instead after long holding time. Only when an appropriate interface microstructure was achieved by optimizing the bonding parameters, could the shear strength of the joint reach 80% of that of the TiAl base alloy.
参考文献
| [1] | P. He;J. C. Feng;B. G. Zhang .A new technology for diffusion bonding intermetallic TiAl to steel with composite barrier layers[J].Materials Characterization,2003(1):87-92. |
| [2] | P. He;J.C. Feng;B.G. Zhang .Microstructure and strength of diffusion-bonded joints of TiAl base alloy to steel[J].Materials Characterization,2002(5):401-406. |
| [3] | X. -W. Du;Jing Zhu;X. Zhang;Z. Y. Cheng;Y. -W. Kim .Composition change during creep in colonies oriented for easy-slip of Ti-46.5Al-2Cr-3Nb-0.2W[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):131-135. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%