Effect of austempering on the transformation induced plasticity (TRIP) of hot rolled multiphase steel was investigated. Polygonal ferrite, granular bainite, and a large amount of stabilized retained austenite could be obtained in the hot rolled multiphase steel. Strain induced martensite transformation (SIMT) of retained austenite and TRIP effectively occur under straining owing to austempering after hot rolling, and mechanical properties of the present steel remain at a relatively high constant value for austempering at 400℃. The mechanical properties of the steel exhibited a good combination of tensile strength (791MPa) and total elongation (36%) because the stability of retained austenite is optimal when the steel is held for 20min.
参考文献
| [1] | V F Zackay;E R Parker;D Fahr;R.Bush .[J].Trans Asm,1967,60:252. |
| [2] | Y Sakuma;O Matsumura;H Takechi .[J].Metallurgical Transactions,1991,22A:489. |
| [3] | O Matsumura;Y Sakuma;H Takechi .[J].ISIJ International,1987,27:570. |
| [4] | O Matsumura;Y Sakuma;H Takechi .[J].ISIJ International,1992,32:1014. |
| [5] | Z Li;D Wu .[J].ISIJ International,2006,46(01):121. |
| [6] | Z.Li,D.Wu.EFFECTS OF TEST TEMPERATURE AND STRAIN RATE ON THE MECHANICAL PROPERTIES IN AN INTERCRITICALLY HEAT-TREATED BAINITE-TRANSFORMED STEEL[J].金属学报（英文版）,2004(06):840-848. |
| [7] | Z.LI,D.Wu.MECHANICAL PROPERTIES IN AN INTERCRITICALLY HEAT-TREATED BAINITE-TRANSFORMED 2%Si STEEL[J].金属学报（英文版）,2004(05):725-731. |
| [8] | K I Sugimoto;M Misu;M Kobayashi;H.Shirasawa .[J].ISIJ International,1993,33:775. |
| [9] | K Sugimoto;M Kobayashi;S Hashimoto .[J].Metallurgical Transactions,1992,23A:3085. |
| [10] | A Z Hanzaki;P D Hodgson;S Yue .[J].ISIJ International,1995,35:324. |
| [11] | E. V. Pereloma;I. B. Timokhina;P. D. Hodgson .Transformation behaviour in thermomechanically processed C-Mn-Si TRIP steels with and without Nb[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(0):448-452. |
| [12] | E Girault;P Jacques;P Harlet;K.Mols,J.Van Humbeek,E.Aernoudt,F.Delannay .[J].Materials Characterization,1998,40:111. |
| [13] | R L Miller .[J].Trans Asm,1964,57:892. |
| [14] | I. B. TIMOKHINA;P. D. HODGSON;E. V. PERELOMA .Effect of Deformation Schedule on the Microstructure and Mechanical Properties of a Thermomechanically Processed C-Mn-Si Transformation-Induced Plasticity Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2003(8):1599-1609. |
| [15] | N C Goel;J P Chakravarty;K Tangri .[J].Metallurgical Transactions,1987,18A(05) |
| [16] | H K D H Bhadeshia;D V Edmonds .[J].Metallurgical Transactions,1979,10A:895. |
| [17] | S W Thompson;D J Colvin;G Krauss .[J].Metallurgical Transactions,1990,21A:1493. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%