综述了保温层下腐蚀(CUI)的研究状况,围绕CUI机理和影响因素展开.重点归纳和阐明了针对CUI问题开展的研究,包括目前的主要研究成果、CUI实验模拟以及检测技术.
The research on corrosion metallic materials beneath insulation(GUI) coat is summarized in this paper.The mechanism and influential factors about CUI are discussed in detail.The recent research progress of CUI is emphasized,including the main research results,experimental simulation and detection technology about CUI.
参考文献
[1] | Fitzgerald B J, Stefan W. A Corrosion under insulation prevention strategy for petrochemical industry piping[J]. Corros. Management, 2004, 57: 15. |
[2] | 梁成浩.现代腐蚀科学与防护技术[M].上海:华东理工大学出版社,2007. |
[3] | 翟金坤.金属高温腐蚀[M].北京:北京航空航天大学出版社,1994. |
[4] | Pollock W I, Barnhart J M. Corrosion of metals under thermal insulation-ASTM special technical publication 880[R]. Philadelphia, Pennsylvania: ASTM, 1985. |
[5] | Kumar M S, Sujata M, Venkataswamy M A, et al. Failure analysis of a stainless steel pipeline[J]. Eng. Failure Anal., 2008, 15: 497. |
[6] | Ali B, Saud A S. Under insulation stress corrosion crack- ing of process piping[A]. Corrosion 2006 Conference & Expo[C]. HT: NACE, 2006. Paper No.06500. |
[7] | Delahunt J F. Corrosion under thermal insulation and fire- proofing an overview[A]. Corrosion/2003[C]. HT: NACE, Paper No.03022, 2003. |
[8] | Kane R D, Ashbaugh W G, McGowan N, et al. New Indus- try Standards, Test Procedures, and Surface Treatments Combat Corrosion under Insulation[A]. Corrosion source- 2000 Online SvmDosium[C]. Paner 0403, 2000. |
[9] | Norsworthy R, Dunn P J. Corrosion under thermal insu- lation[J]. Coat. Linings, 2002. |
[10] | Frank D V. Corrosion under insulation[J]. Process Safety Prog., 2009, 28(1): 3. |
[11] | Ahluwalia H S. CUI: an in-depth analysis[J]. Insulation Outlook, 2006. |
[12] | ASTM C 692, Standard test method for evaluating the in- fluence of thermal insulations on external stress corrosion cracking tendency of austenitie stainless steel[S]. |
[13] | ASTM C 871, Standard test methods for chemical analy- sis of thermal insulation materials for leachable chloride, fluoride, silicate, and sodium ions[S]. |
[14] | ASTM C 795, Standard specification for thermal insula- tion for use in contact with austenitic stainless steel[S]. |
[15] | ASTM C 929, Standard practice for handling, transport- ing, shipping, storage, receiving, and application of ther- mal insulation materials for use in contact with austenitic stainless steel[S]. |
[16] | Winnik S. Corrosion under insulation (CUI) guidelines [M]. UK: Woodhead Publishing Limited and Maney Pub- lishing Limited on behalf of The Institute of Materials, Minerals & Mining, 2008. |
[17] | Abavarathna D, Ashbaugh W G, Kane R D, et al. Mea- surement of corrosion under insulation and effectiveness of protective coatings[A]. NACE International, 1997. |
[18] | Richardson J, Fitzsimmons T. Use of aluminium foil for prevention of stress corrosion cracking of austenitic stain- less steel under thermal insulation[A]. ASTM STP 880[C]. Philadelphia, Pennsylvania: ASTM, 1985. |
[19] | Richert J P. Issues surrounding insulated SS and cracking under thermal insulation-refinery experiences in tropical environments'piping[A]. Corrosion/2003[C]. NACE, Paper 03026. 2003. |
[20] | 李君.保温层下防腐保护及冷喷铝技术[J].上海涂料,2008,46(6):19. |
[21] | A state of the art report on protective coatings for carbon steel and austenitic stainless steel surfaces under thermal insulation and cementations fireproofing[A]. NACE[C], 1989. |
[22] | Fischer K P, Thomason W H, Rosbrook T, et al. Perfor- mance history of thermal-sprayed aluminum coatings in offshore service[J]. Mater. Perform., 1995, 34(4), 27. |
[23] | Halliday M. Preventing corrosion under insulation-new generation solutions for an age old problem[A]. Corrosion &Prevention 2006[C]. Paper No. 014, 2006. |
[24] | Abayarathna D,任中华译.保温层下的腐蚀及涂层保护度的测量[J].国外油田工程,2000,10:46. |
[25] | European Meeting on Corrosion under Lagging, Newcastle upon Tyne, UK, 1980. |
[26] | NACE RP0198-1998, The control of corrosion of metals under thermal insulation and fireproofing materials-A sys- tems approach[S]. |
[27] | NACE RP0198-2004, The control of corrosion of metals under thermal insulation and fireproofing materials-A sys- tems approach[S]. |
[28] | Corrosion under Insulation-Have you a Problem?[C]. London: Institute of Materials, Minerals and Mining, 2004. |
[29] | ASTM G189-07, Standard guide for laboratory simulation of corrosion under insulation[S]. |
[30] | 杨文冬,黄剑锋,曹丽云等.高温防护涂层的研究进展及发展趋势[J].材料保护,2009,42(1):40. |
[31] | McGowan N, Abavarathna D, Heimannn B, et al. In- novation and environmentally benign solution for corro- sion under insulation (C.U.I.) for steam process piping[R]. NAVSEA, 1996. |
[32] | Kane R D, Chauviere M. Evaluation of steel and TSA coating corrosion under insulation (CUI) environ- ment[R]. NACE Corrosion 2008 Conference &: Expo., Paper No.08036, 2008. |
[33] | De Sousa F V V, Da Mota R O, Quintela J P, et al. Characterization of corrosive agents in polyurethane foams for thermal insulation of pipelines[J]. Electrochim. Acta, 2007, 52: 7780. |
[34] | Choi Y S, Chung M K, Kim J G. Effects of cyclic stress and insulation on the corrosion fatigue properties of ther- mally insulated pipeline[J]. Mater. Sci. Eng., 2004, A384: 47. |
[35] | Galbraith JM,任中华译.检测管线保温层下腐蚀的新技术[J].国外油田工程,2002,18(3):53. |
[36] | Aung N N, Wai W K, Tan Y J . A novel electrochemi- cal method for monitoring corrosion under insulation[J]. Anti-Corros. Methods Mater., 2006, 53(3): 175. |
[37] | Abdullah J, Yahya R. Application of CdZnTe gamma-ray detector for imaging corrosion under insulation[J]. Solid State Sci. Technol., 2006, 99: 74. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%