采用电化学测试技术、X射线衍射等技术研究了Ti0.8Zr0.2V1.6Mn0.8.xCrxNi0.6(0≤x≤0.64)贮氢电极合金的结构和电化学放电特性.研究表明:合金由C14 Laves相和BCC相构成;铬替代锰的量越多,枝晶组织越粗大.X射线衍射发现替代影响合金的晶格参数.合金的最大电化学放电容量为545 mAh/g,电化学活化容易,但循环性能比较差.随着替代量增大,由于铬抑制了钛、锆和钒元素的表面迁移和氧化使合金的循环性能退化明显减轻,但同时因为替代使晶胞过大导致最大电化学放电容量有所降低.
参考文献
| [1] | Ovshinsky S R;Fetcenko M A;Ross J .[J].科学(上海),1993,260:176. |
| [2] | 江建军,雷永泉,孙大林.提高AB5型贮氢合金电极材料循环寿命的途径[J].稀有金属材料与工程,1993(03):68-74. |
| [3] | 王福山,王春生,陈立新.（Ti0.7Zr0.2V0.1）Ni贮氢合金的电化学性能及氢致相变研究[J].稀有金属材料与工程,1999(02):73-76. |
| [4] | Gamv T;Moriwaki Y;Yanagihara N;Iwaki T.[J].Journal of Hydrogen Energy,1985(10):39. |
| [5] | Moriwaki Y;Gamo T;Iwaki T .[J].Journal of the Less-Common Metals,1991,1028:172-174. |
| [6] | Lee Hanho;Lee Kiyoung;Lee Jaiyoung .[J].Journal of Alloys and Compounds,1996,239:63. |
| [7] | Au Ming;Poruauian F;Sinizu S;Sankar S G, Zhang Lian .[J].Journal of Alloys and Compounds,1995,223:1. |
| [8] | Yu Jisang;Lee Kiyoung;Lee Jaiyoung .[J].Journal of Alloys and Compounds,1997,259:270. |
| [9] | Jung Jaehan;Lee Hanho;Kim Dongmyung et al.[J].Journal of Alloys and Compounds,1998,266:266. |
| [10] | Gutjahr M A;Buchner H;Beccu K D;Saufferer H .[J].Journal of Power Sources,1973,4(79):5. |
| [11] | XU Yan-hui,CHEN Chang-pin,LI Shou-quan,YING Tiao,WANG Qi-dong.High-temperature electrochemical performance and |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%