Fatigue behaviors of Z2CND18.12N stainless steel under thermal-mechanical cycling

金属学报(英文版), 2011, 24(2): 101-108.

^1, , ^2, , ^3, , ^4, , ^5, , ^6,

1.School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China

2.School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China

3.Suzhou Nuclear Power Institute, Suzhou 240051, China

4.Suzhou Nuclear Power Institute, Suzhou 240051, China

5.Key Laboratory of Efficient & Clean Energy Utilization, College of Hunan Province, Changsha University of Science and Technology, Changsha 410114, China

6.School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China

基金项目: Key Laboratory of Efficient & Clean Energy Utilization,College of Hunan Province,is acknowledged(2010NGQ003) PhD Programs Foundation of Ministry of Education of China(20090032110016) the National High Technical Research and Development Program of China(2009AA04Z403)

Fatigue behaviors of Z2CND18.12N stainless steel under thermal-mechanical cycling

Liubing WANG ^1, , Dunji YU ^2, , Fei XUE ^3, , Weiwei YU ^4, , Jian CHEN ^5, , Xu CHEN ^6,

1.School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China

2.School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China

3.Suzhou Nuclear Power Institute, Suzhou 240051, China

4.Suzhou Nuclear Power Institute, Suzhou 240051, China

5.Key Laboratory of Efficient & Clean Energy Utilization, College of Hunan Province, Changsha University of Science and Technology, Changsha 410114, China

6.School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China

Keywords： Thermomechanical fatigue

Tests under mechanical strain control were performed to investigate the TMF behavior of Z2CND18.12N within the temperature range between 150-550 ℃. Differentstrain amplitudes and phase-angles were applied. Total strain controlled low cycle fatigue test was also performed at the peak temperature of TMF cycling. The results show that the cyclic stress response of the material displayed an initial hardening regime followed by a saturation period and then cyclic softening till failure. The TMF cycling leads to the development of significant amounts of mean stress. Some life prediction models were employed to predict the TMF life of Z2CND18.12N, and the results indicate that the energy-based models provide good prediction on the thermal-mechanical fatigue behaviors of this material. An optical microscopic observation shows that the surface crack initiations and crack propagations are typicallytransgranular mode.

参考文献

[1]	H. Samrout;R. EI Abdi .Fatigue behaviour of 28CrMoV5-08 steel under thermomechanical loading[J].International Journal of Fatigue,1998(8):555-563.
[2]	S. L. Mannan;M. Valsan .High-temperature low cycle fatigue, creep-fatigue and thermomechanical fatigue of steels and their welds[J].International Journal of Mechanical Sciences,2006(2):160-175.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Fatigue behaviors of Z2CND18.12N stainless steel under thermal-mechanical cycling

参考文献