研究单体浓度（AM）、单体/交联剂比例（AM/MBAM）、反应温度和固相体积分数等工艺条件对氧化铍凝胶注模坯体强度的影响,并从自由基聚合反应角度分析各因素对纯凝胶强度和均匀性的影响的原因,得出各因素较合适的参数范围。结果表明纯凝胶和坯体强度随着单体浓度的增加而增加,但过高的单体浓度会使结构均匀性变差,因此单体浓度较合适的范围为10%～20%（质量分数）;随着AM/MBAM比例的增加,坯体强度降低,均匀性下降,AM/MBAM比例应控制在20∶1与30∶1之间;随着反应温度的升高,凝胶强度起初逐渐减低而后又升高,但凝胶均匀性则为先逐渐增加而后又减低,反应温度应控制在20～35℃范围内;随着固相体积分数的增加,凝胶注模坯体强度逐渐下降,但均匀性却升高,因此在满足坯体强度要求的前提下,固相体积分数应尽可能的较高。
The effect of process conditions（monomer concentration,monomer/crosslinker ratio,reaction temperature and solids loading of suspension）on strength of green body prepared by gelcasting was investigated.The change reason of the strength and homogenization of pure gels was analyzed based on free-radical polymerization theory,and the ranges of each process parameters were achieved.The results show：the strength of pure gel and green body increase with increasing monomer concentration,but the homogenization of these prepared with higher monomer concentration are decreased,and thus monomer concentration should be between 10% and 20%（mass fraction）;increasing the ratio between AM and MBAM,the strength and homogenization of gel decrease,and so the ratio between AM and MBAM is between 20∶1 and 30∶1;as the reaction temperature rises,the strength of gels enhance firstly and then decrease,but vice versa the homogenization of these,therefore,the reaction temperature lies between 20℃ and 30℃;the strength of green body reduce but homogenization increase with solids loading,and so the solids loading of suspensions for green body with enough strength should be as much high as possible.
参考文献
| [1] | Adolfsson E .Gelcasting of zirconia using agarose[J].Journal of the American Ceramic Society,2006(6):1897-1902. |
| [2] | Manjiang Dong;Xiaojian Mao;Zhaoquan Zhang .Gelcasting of SiC using epoxy resin as gel former[J].CERAMICS INTERNATIONAL,2009(4):1363-1366. |
| [3] | 杜景红,史庆南,严继康,孙加林.凝胶注模在PMN-PZT压电陶瓷中的应用[J].功能材料,2005(08):1229-1231. |
| [4] | 王小锋,王日初,彭超群,李婷婷,罗玉林,王超,刘兵.凝胶注模成型技术的研究与进展[J].中国有色金属学报,2010(03):496-509. |
| [5] | M.A. Janney;W. Ren .Gelcast tooling: net shape casting and green machining[J].Materials and Manufacturing Processes,1998(3):389-403. |
| [6] | 王艳香,孙健,余熙.碳化硅材料凝胶注模成型工艺的研究[J].硅酸盐通报,2007(06):1202-1206. |
| [7] | 王亚利,郝俊杰,郭志猛.凝胶注模成型生坯强度影响因素的研究[J].材料科学与工程学报,2007(02):262-264. |
| [8] | 仝建峰,陈大明,李宝伟,刘晓光.凝胶注模氧化铝陶瓷坯体的结构与表征[J].航空材料学报,2004(06):42-46. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%