采用溶胶-凝胶法,在设计的反应体系中制备了锐钛矿型氧化钛溶胶,并采用浸渍提拉法在载玻片上成膜,无需常见研究中的高温热处理,即可获得锐钛矿型氧化钛薄膜.将氧化钛溶胶在40℃烘干后进行XRD测试,发现氧化钛粉末为锐钛矿型结构.对薄膜的扫描电镜分析,发现薄膜中存在片状的锐钛矿晶体.片晶的宽度约30 nm,长度从200 nm～1 μm不等.由于含有片状的锐钛矿晶体,所得的氧化钛薄膜可在紫外线激发下降解罗丹明B.光催化反应进行120 min时,罗丹明B的降解率达到45%.
By means of sol-gel method,TiO2 sol containing anatase crystalline grains was synthesized in a designed reaction system.So anatase TiO2 film was prepared by dip-coating technique at room temperature without traditional high-temperature heat treatment.X-Ray Diffraction(XRD)analysis for the powders from the drying sol at 40℃reveals that the phase of powders belongs to an anatase structure.In Scanning Electron Microscopy(SEM)images of the film,there are anatase flake crystals with 30 nm in width,while the length changes from 200 nm to 1 μm.The film,containing flake anatase crystals,can decompose Rhodamine B at a rate of 45%after UV irradiation for 120min.
参考文献
| [1] | 高基伟,丁新更,黄顺余,杨辉.热处理温度对TiO2结构和光学性能的影响[J].稀有金属材料与工程,2004(z1):52-54. |
| [2] | Miao L;Tanemura S;Kondo Y.[J].Applied Surface Science,2004(238):125. |
| [3] | Ding Xingeng;Yang Hui .[J].Key Engineering Materials,2005,280-283(01):801. |
| [4] | Fujishima A;RAO T N;Tryk D A .[J].Journal of Photochemistry and Photobiology C:Photochemistry Reviews,2000,1(01):1. |
| [5] | Sakai N.;Fujishima A.;Watanabe T.;Hashimoto K.;Wang R. .Effect of ultrasonic treatment on highly hydrophilic TiO2 surfaces[J].Langmuir: The ACS Journal of Surfaces and Colloids,1998(20):5918-5920. |
| [6] | Linsebigler A L;Lu G Q;Yates J T .[J].Chemical Reviews,1995,95(03):735. |
| [7] | Gao Jiwei;Shen Qianhong;Fang Ming et al.[J].Key Engineering Materials,2007,336-338:2350. |
| [8] | Gao Jiwei;Yang Hui;Shen Qianhong .[J].Electronic Components & Materials,2006,25(08):39. |
| [9] | 方明,高基伟,申乾宏,王平,杨辉.锐钛矿晶型TiO2溶胶的精细结构及其光催化活性[J].硅酸盐学报,2006(04):438-441. |
| [10] | 杨辉,申乾宏,高基伟.TiO2-PEDT/PSS双层复合膜的制备及其光催化性能[J].催化学报,2005(10):839-841. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%