主要研究了钒钛基脱硝催化剂失活机理及再生。采用SEM、EDS、XRD、BET等手段对国内某家燃煤火电厂运行20000h的SCR脱硝催化剂进行表征,然后使用0.5mol/L的硫酸和0.01mol/L的氢氟酸对运行过的催化剂进行了清洗再生并通过烟气模拟-催化剂活性测试系统考察了催化剂的脱硝活性。结果表明,相比于新鲜催化剂,运行后的催化剂活性明显下降,孔容和比表面积有所下降,其表面存在着组成复杂的飞灰,飞灰主要成分为SiO2;采用0.01mol/L氢氟酸溶液清洗能够明显恢复催化剂的脱硝活性,这是因为氢氟酸可以有效清除失活催化剂表面的SiO2。
Deactivation and regeneration of V2O5/TiO2 catalyst for elimination of NO were studied, lhe spent V2O5/TiO2 catalyst sample was from a domestic power plant, which had been operated for 20000h. The spent V2O5/TiO2 catalyst was characterized by SEM, EDS, XRD and BET techniques to reveal the deactivation mechanism. The regeneration of V2 O5/TiO2 catalyst was conducted by washing with aqueous solution of 0.5 mol/L H2SO4 or 0.01mol/L HF. The results showed that the actvity of the spent catalyst dropped greatly in comparison with the fresh catalyst. The reason was that the spent catalyst was heavily covered by ash which blocked the active sites and plugged the pores. After the spent catalyst was washed with aqueous solutions of 0.01mol/L HF, the activity of regenerated catalyst was improved significantly due to effective removal of sili- con dioxide covered on the spent catalyst, a main composition of the ash.
参考文献
| [1] | Hsu Liyeh;Teng Hsisheng .Influence of thermal treat- ment on the catalytic activity of Cuqoaded carbons in NO reduction with NHa and regeneration of the thermally de activated catalysts[J].Applied Catalysis B:Environmental,2003,42:69-76. |
| [2] | 陈进生.火电厂烟气脱硝技术选择性催化还原法[M].北京:中国电力出版社,2008:2. |
| [3] | 周涛,刘少光,唐名早,陈成武,徐玉松,吴进明.选择性催化还原脱硝催化剂研究进展[J].硅酸盐学报,2009(02):317-324. |
| [4] | 强华松,刘清才.燃煤电厂SCR脱硝催化剂的失活与再生[J].材料导报,2008(z3):285-287. |
| [5] | 杨眉,刘清才,薛屺,高英.化学气相沉积制备V2O5-WO3/TiO2催化剂及表征[J].功能材料,2010(04):683-686. |
| [6] | 赵毅,朱振峰,贺瑞华,胡峻涛,李军奇.V2O5-WO3/TiO2基SCR催化剂的研究进展[J].材料导报,2009(01):28-31. |
| [7] | 满雪,高维恒.SCR脱硝催化剂的研究现状及展望[J].广州化工,2008(06):22-24. |
| [8] | Wang Zaihua;Li Xingjun;Song Wenji et al.The effects of Ag doped to the Ag-V/Ti02 catalysts with low vanadi um loadings for DENO[J].Journal of Functional Materi als,2011,42(09):1610-1618. |
| [9] | Zhang Y J;Jensen A D;Johnsson J E .Deactivation of V2O5-WO3-TiO2 SCR catalyst at a biomass fired corn bined heat and power plant[J].Applied Catalysis B:Environmental,2005,60:253-264. |
| [10] | Xianlong Zhang;Zhanggen Huang;Zhenyu Liu .Effect of KCl on selective catalytic reduction of NO with NH3 over a V2O5/AC catalyst[J].Catalysis Communications,2008(5):842-846. |
| [11] | L. Baxter .Biomass-coal co-combustion: opportunity for affordable renewable energy[J].Fuel,2005(10):1295-1302. |
| [12] | Jens Beck;Jurgen Brandenstein;Sven Unterberger;Klaus R.G.Hein .Effects of sewage sludge and meat and bone meal Co-combustion on SCR catalysts[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2004(1):15-25. |
| [13] | Benson S A;Laumb J D;Crocker C R et al.SCR cata lyst performance in flue gases derived from subbitumi nous and lignite coals[J].Fuel Proc T,2005,86:577-613. |
| [14] | Xiaoping Xuan;Changtao Yue;Shuyuan Li .Selective catalytic reduction of NO by ammonia with fly ash catalyst[J].Fuel,2003(5):575-579. |
| [15] | Raziyeh Khodayari;C.U.Ingemar Odenbrand .Regeneration of commercial SCR catalysts by washing and sulphation: effect of sulphate groups on the activity[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2001(4):277-291. |
| [16] | Khodayari R.;Odenbrand CUI. .Regeneration of commercial TiO2-V2O5-WO3SCR catalysts used in bio fuel plants[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2001(1/2):87-99. |
| [17] | Hartenstein;Hans-Ulrich .Hoffmann Thies[P].USP:7741239,2010. |
| [18] | 李云涛,毛宇杰,钟秦,曲虹霞,王娟.SCR催化剂的组成对其脱硝性能的影响[J].燃料化学学报,2009(05):601-606. |
| [19] | 陈进生.火电厂烟气脱硝技术一选择性催化还原法[M].北京:中国电力出版社,2008:201. |
| [20] | Kobayashi M;Kuma R;Morita A .Low temperature se- lective catalytic reduction of NO by NH3 over Vz 05 sup- ported on TiO2-SiO2-MoO3[J].Catalysis Letters,2006,112(1-2):37-44. |
| [21] | Zhang He;Han Jian;Niu Xiaowei et al.Study of syn- thesis and catalytic property of WO3/TiO2 catalysts for NO reduction at high temperatures[J].Journal of Molecular Catalysis A:Chemical,2011,350(1-2):35-39. |
| [22] | Joshua R. Strege;Christopher J. Zygarlicke;Bruce C. Folkedahl;Donald P. McCollor .SCR deactivation in a full-scale cofired utility boiler[J].Fuel,2008(7):1341-1347. |
| [23] | 陈进生.火电厂烟气脱硝技术-选择性催化还原法[M].北京:中国电力出版社,2008:51. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%