以WC-9Ni-0.57Cr硬质合金为研究对象,采用失重法、电化学测试、力学性能测试和显微形貌分析等方法,研究合金在3.5%NaCl模拟海水溶液中的腐蚀行为,并与传统的WC-6Co硬质合金进行了比较.结果表明:在3.5%NaCl溶液中室温腐蚀8周的WC-gNi-0.57Cr合金与WC-6Co合金的腐蚀速率分别为0.0033mm/a和0.0072mm/a,以Ni-Cr为粘结相制备的硬质合金耐腐蚀性能明显优于传统的WC-Co硬质合金,具有较强的抗腐蚀能力;硬质合金微观腐蚀形态表现为粘结相的腐蚀,使力学性能降低,室温腐蚀4周后WC-9Ni-0.57Cr合金与WC-6Co合金的横向断裂强度损失率分别为8.43%和31.14%.
参考文献
| [1] | 李琴.浅论机械密封中摩擦副材料的选择[J].化工设计通讯,2002(04):52-55. |
| [2] | Sutha Sutthiruangwong;Gregor Mori .Corrosion properties of Co-based cemented carbides in acidic solutions[J].International Journal of Refractory Metals & Hard Materials,2003(3/4):135-145. |
| [3] | S. Hochstrasser(-Kurz);Y. Mueller;C. Latkoczy;S. Virtanen;P. Schmutz .Analytical characterization of the corrosion mechanisms of WC-Co by electrochemical methods and inductively coupled plasma mass spectroscopy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(4):2002-2020. |
| [4] | 胡道平,何宝山,孔德会.Cr含量对WC基硬质合金耐腐蚀性能的影响[J].腐蚀与防护,2006(08):382-386,421. |
| [5] | 孔德会,何宝山,刘林海.Cr含量对WC基硬质合金组织和性能的影响[J].上海有色金属,2005(02):53-56,85. |
| [6] | 王兴庆,李晓东,郭海亮,何宝山.Al含量对WC-Co硬质合金耐腐蚀性能的影响[J].粉末冶金材料科学与工程,2006(04):219-224. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%