以十二烷基硫酸钠（SDS）和聚乙二醇-400（PEG-400）为乳化剂,采用半连续乳液聚合法制备了丙烯酸六氟丁酯（HFBA）-丙烯酸丁酯（BA）-甲基丙烯酸甲酯（MMA）共聚物乳液,考察了丙烯酸丁酯与甲基丙烯酸甲酯摩尔比对乳液所成薄膜力学性能及耐水性的影响,并优化了丙烯酸六氟丁酯的用量。结果表明,薄膜的抗张强度随BA与MMA摩尔比的减小而增大,耐水性增强,但断裂伸长率降低;薄膜的耐水性随着氟单体用量的增大而增强。SEM-EDS显示含氟组分易向薄膜-空气界面迁移;接触角测定结果表明加入氟单体后薄膜表面与水的接触角增大。
The fluorine-containing polyacrylate latex with poly （hexafluorobutyl acrylate-co-butyl acrylate-co- methyl methacrylate） was developed by semi-continuous emulsion polymerization using sodium dodecyl sulfate SDS and poly（ethylene glycol） as emulsifier. The mechanical properties and water-resistance of films synthe- sized by different molar ratio of BA and MMA were studied. The amount of HFBA was ultimately optimized. The dosage of MMA increased, the tensile strength and the water-resistance of films were improved, whereas the breaking elongations were decreased. In addition, the introduction of fluorine had contributed greatly to the water-resistance of films. Scanning electron microscope （SEM） and energy dispersive spectroscopy （EDS） proved that fluorine has transferred to the surfaces. Contact angle revealed that the contract angle of films in- creased with the incorporation of fluorine.
参考文献
| [1] | 马建中;兰云军;强西怀.制革整饰材料化学[M].北京:中国轻工业出版社,1998:303-382. |
| [2] | 任小亮 .梳状有机硅改性丙烯酸树脂的研究[D].山东轻工业学院,2010. |
| [3] | 杨玉玮 .有机硅改性丙烯酸树脂的研究[D].西北工业大学,2007. |
| [4] | 周建华,马建中,王立.核壳型有机硅改性丙烯酸树脂织物涂层剂的研制[J].陕西科技大学学报（自然科学版）,2008(03):39-44. |
| [5] | 马建中,王华金,鲍艳.核壳型硅丙复合乳液的合成及其性能研究[J].精细化工,2010(02):195-200. |
| [6] | 周建华,马建中,王立.核壳型有机硅改性丙烯酸酯乳液皮革涂饰剂的合成研究[C].中国化工学会精细化工专业委员会第103次学术会议暨2007全国皮革化学品学术研讨会论文集,2007:277-283. |
| [7] | 马建中,张志杰,刘凌云,胡静.丙烯酸树脂/纳米SiO2复合涂饰剂的合成研究[J].皮革科学与工程,2005(02):8-11,27. |
| [8] | 胡静,马建中,管建军.无皂丙烯酸树脂/SiO2纳米复合皮革涂饰剂的研究[J].涂料工业,2006(08):8-12,16. |
| [9] | 王川,廖学品,石碧.氟化丙烯酸树脂涂饰剂的合成、表征及应用[J].中国皮革,2007(13):40-44,47. |
| [10] | 和玲,梁军艳,高敏,朱江安,徐岩.333水性核壳结构型含氟丙烯酸酯乳液的合成及性能[J].高分子材料科学与工程,2007(01):120-124. |
| [11] | 陈中华,赵秀娟.氟化丙烯酸酯共聚乳液的研究进展[J].涂料工业,2007(09):57-60. |
| [12] | 唐敏锋,范晓东,刘涛,刘祥.含氟丙烯酸酯核壳乳液的合成与性能[J].高分子材料科学与工程,2007(02):99-102. |
| [13] | Landfester K.;Rothe R.;Antonietti M. .Convenient synthesis of fluorinated latexes and core-shell structures by miniemulsion polymerization[J].Macromolecules,2002(5):1658-1662. |
| [14] | Misra, A;Jarrett, WL;Urban, MW .New Poly(methyl methacrylate)/n-Butyl Acrylate/Pentafluorostyrene/Poly(ethylene glycol) (p-MMA/nBA/PFS/PEG) Colloidal Dispersions: Synthesis, Film Formation, and Protein Adsorption[J].Macromolecules,2009(19):7299-7308. |
| [15] | 张珍英,管蓉,陈正国.含氟乳化剂丙烯酸酯乳液的制备及性能[J].胶体与聚合物,2001(01):11-13,17. |
| [16] | LI-HONG LIU;MINGDI YAN .Perfluorophenyl Azides: New Applications in Surface Functionalization and Nanomaterial Synthesis[J].Accounts of Chemical Research,2010(11):1434-1443. |
| [17] | 肖新颜,杜沛辉,万彩霞,张会平.含氟丙烯酸酯聚合物乳液的合成及涂膜性能研究[J].新型建筑材料,2007(11):36-39. |
| [18] | 赵兴顺,丁小斌,郑朝晖,潘毅,朱珠,戴静,彭宇行.含氟丙烯酸酯共聚乳液的制备及表征[J].功能高分子学报,2003(04):436-440. |
| [19] | 赵兴顺,丁小斌,张军华,郑朝晖,潘毅,朱珠,彭宇行.含氟丙烯酸酯共聚乳液及其膜表面特性的研究[J].高分子学报,2004(02):196-200. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%