采用XRD、SEM等表征方法研究钨丝增强(Zr41.2Ti13.8Cu12.5Ni10Be22.5)100-xNbx非晶复合材料的力学行为.研究表明,分别加入x=1,3,5,7(atA)的Nb后,制备的复合材料试样基体仍为非晶态:随Nb含量的增加,钨丝增强(Zr41.2Ti13.8Cu12.5Ni10Be22.5)100-xNbx非晶复合材料的压缩屈服强度提高,塑性应变也随之提高.x=7时,复合材料具有良好的综合性能,压缩屈服强度达2450 MPa,塑性应变达20%.
Mechanical properties of(Zr41.2Ti13.5Cu12.5Ni10Be22.5)100-xNbx bulk metallic glass(BMG)matrix composites reinforced by tungsten fiber(Wf)were investigated by X-ray diffraction, scanning electron microscope(SEM)and so on. The results show that the matrix of the prepared composites remain amorphous after adding Nb with x=1, 3, 5 and 7, at%, and the compressive yield strength and plastic strain increase with the increase of Nb content. The composites with x=7 possess the excellent comprehensive properties, whose compressive yield strength and plastic strain reach 2450 MPa and 20%, respectively.
参考文献
| [1] | Leng Y;Courtney T H .[J].Journal of Materials Science,1991,26:588. |
| [2] | R.D.Conner;R.B.Dandliker;W.L.Johnson .Mechanical properties of tungsten and steel fiber reinforced Zr-41.25Ti_13.75Cu_12.5Ni_10Be_22.5 metallic glass matrix composites[J].Acta materialia,1998(17):6089-6102. |
| [3] | Dandliker R B;Conner R D;Johnson W L .[J].Journal of Materials Research,1998,13(10):2839. |
| [4] | Choi-Yim H;Conner R D;Szuecs F et al.[J].Scripta Materialia,2001,45:1039. |
| [5] | Conner R D;Dandliker R B;Scruggs V et al.[J].International Journal of Impact Engineering,2000,24:435. |
| [6] | Ji Yingfei;Ma Xueming;Dong Yuanda et al.[J].Materials Science and Engineering,2000,18(03):39. |
| [7] | Bang F;Chen G;Li W L et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2008,39A:1812. |
| [8] | 王美玲,惠希东,董伟,刘雄军,陈国良.钨丝增强ZrTiCuNiBeNb金属玻璃基复合材料界面[J].中国有色金属学报,2004(10):1632-1636. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%