采用二甲苯和二茂铁作为碳源和催化剂的化学气相沉积法连续制备定向碳纳米管阵列,在反应6h内获得长度为6mm的宏观定向碳纳米管阵列.当反应时间超过6h后,定向碳纳米管阵列的生长速度明显下降,并有停止生长的趋势,反应16h,定向碳纳米管阵列的厚度仅为6.7mm.本文研究了采用多次连续进给碳源和催化剂的方式制备定向碳纳米管阵列,成功的制备了8.9mm厚的定向碳纳米管阵列,阵列中的碳纳米管具有高的定向性和良好的界面结合.
参考文献
| [1] | Saito R;Dresselhaus G;Dresselhaus M S.Physical Properties of Carbon Nanotubes[M].London: Imperial College Press,1998 |
| [2] | Heer WA;Chatelain A;Ugarte D .[J].科学(上海),1995,270(5239):1179-1180. |
| [3] | Li W Z;Xie S;Qian L X.[J].科学(上海),1996(274):1701-1703. |
| [4] | Eres G;Puretzky A A;Geohegan D B et al.[J].Applied Physics Letters,2004,84(10):1759-1761. |
| [5] | Ren Z F;Huang Z P;Xu J W.[J].科学(上海),1998(282):1105-1107. |
| [6] | Andrews R;Jacques D;Rao A M et al.[J].Chemical Physics Letters,1999,303(526):467-474. |
| [7] | 曹宗良,王健农,丁冬雁,戴杰华,余帆.化学气相沉积法快速生长定向纳米碳管[J].新型炭材料,2003(01):48-52. |
| [8] | Zhang XF.;Cao AY.;Wei BQ.;Li YH.;Wei JQ.;Xu CL.;Wu DH. .Rapid growth of well-aligned carbon nanotube arrays[J].Chemical Physics Letters,2002(3-4):285-290. |
| [9] | Zhang X F;Cao A Y;Li Y H.Synthesis of macroscopic well-aligned carbon nanotube arrays[A].,2002-09-15 |
| [10] | Feng W;Bai X D;Lian Y Q .[J].炭素,2003,41:1551-1557. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%