利用线性扫描法和循环伏安法分别讨论了镀液中Fe2+和Ni2+浓度、pH值、温度、光亮剂、配位剂含量对Fe-Ni合金电沉积的电化学行为的影响.结果表明,镀液的pH值降低,温度升高时,Fe-Ni合金共沉积的阴极极化减小,镀液中Fe2+浓度增加,Ni2+浓度减小,Fe-Ni合金共沉积的阴极极化增大;加入光亮剂和配位剂时,有利于提高镀层的致密性,同时镀层的耐腐蚀性增强.通过计算Fe-Ni合金共沉积电极反应的表观活化能,阴极电极电势在-1.0～-1.2V时,表观活化能均＞40kJ/mol,说明Fe-Ni合金的共沉积过程为电化学步骤控制.XRD表明Fe-Ni合金为固溶体晶体结构,SEM表明镀层表面光亮平滑.
参考文献
| [1] | Afshar A.;Dolati AG.;Ghorbani M. .Electrochemical characterization of the Ni-Fe alloy electrodeposition from chloride-citrate-glycolic acid solutions[J].Materials Chemistry and Physics,2003(2):352-358. |
| [2] | D. C. Jiles .Recent advances and future directions in magnetic materials[J].Acta materialia,2003(19):5907-5939. |
| [3] | Daheum Kim;D. -Y. Park;B. Y. Yoo;P. T. A. Sumodjo;N. V. Myung .Magnetic properties of nanocrystalline iron group thin film alloys electrodeposited from sulfate and chloride baths[J].Electrochimica Acta,2003(7):819-830. |
| [4] | 李鹏,卢琳,刘天成,孙克,卢志超,卢燕平.Fe-36%Ni软磁合金电沉积条件的研究[J].功能材料,2007(01):32-35. |
| [5] | 杨余芳,龚竹青,罗北平,马玉天,阳征会.电沉积Fe-Ni合金箔的工艺和性能研究[J].电镀与精饰,2006(01):5-9. |
| [6] | Kieling VC .Parameters influencing the electrodeposition of Ni-Fe alloys[J].Surface & Coatings Technology,1997(2/3):135-139. |
| [7] | Yin K M;Jan S L;Lee C C .[J].Surface and Coatings Technology,1996,88(1-3):219-225. |
| [8] | 郭鹤桐;姚素薇.基础电化学及其测量[M].北京:化学工业出版社,2009:209-231. |
| [9] | 胡会利;李宁.电化学测量[M].北京:国防工业出版社,2007:178-204. |
| [10] | Yin K M;Jan S L;Lee C C .[J].Surface and Coatings Technology,1997,88(1-3):219-225. |
| [11] | 方景礼.电镀添加剂--理论与应用[M].北京:国防工业出版社,2007:47-49. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%