针对我国水轮机过流部件长时间运行后表面腐蚀严重这一问题，选用 YG8电极材料对水轮机叶片用0Cr13Ni5Mo不锈钢进行电火花表面强化处理，基于电化学测试技术和交流阻抗测试方法，对强化层的电化学腐蚀性能进行了深入研究。结果表明，强化过程中电极材料与基体材料元素相互熔渗和扩散，强化层内有新的相结构生成，且强化层为冶金结合。与基体材料相比，在腐蚀溶液中电火花强化后试件的自腐蚀电位增大，自腐蚀电流密度减小，试件腐蚀速度变慢，耐腐蚀性能明显提高。
For the abrasion phenomenon of the turbine flowing-passage components was very serious, the electrospark surface strengthening process of stainless steel 0Cr13Ni5Mo by YG8 electrode was carried out in this paper. Based on the electrochemical measurement technique and the electrochemical impedance spectroscopy test method, the electrochemical corrosion properties of strengthening layer is studied. The results show that in the process of strengthening, the electrode materials and substrate material mutual infiltration and melting element diffusion, new phase structure are formed in the strengthening layer, and the strengthening layer is metallurgical combination. In the corroding liquor, the corrosion potential of the strengthening layer increases, the corrosion current density decreases, the corrosion speed slows down, and the corrosion resistance performance of strengthening layer are improved.
参考文献
| [1] | 顾四行;杨天生;闵京声.水机磨蚀[M].北京:中国水利水电出版社,2008:3-14. |
| [2] | 谭宏斌,刘道新,张晓化,鲜宁,管湘芝.2Cr13不锈钢表面电火花强化及磨损和冲蚀行为研究[J].机械科学与技术,2007(05):662-667. |
| [3] | 王者昌,陈静.水轮机抗空蚀磨损金属复层方法、材料和应用[J].焊接,2009(02):38-46. |
| [4] | WANG H X;ZHANG XU;ZHANG W S et al.Finite element numerical simulation of EDM surface strengthening in gas medium of stainless steel 1Cr13[J].Advanced Materials Research,2010,136:189-193. |
| [5] | 王建升.电火花沉积工艺及沉积层性能的研究[J].表面技术,2005(01):27-30. |
| [6] | 王钊,陈荐,何建军,戎雪坤,李石德.电火花表面强化技术研究与发展概况[J].热处理技术与装备,2008(06):46-50. |
| [7] | 张平,马琳,梁志杰,张二亮.便携式电火花沉积镍基合金工艺[J].焊接学报,2011(04):33-36. |
| [8] | WANG H X;ZHANG X .The formation laws and in-fluencing factors of strengthening layer in EDM of stai-ning steel 1Cr13[J].Materials Science Forum,2011,697-698:1-3. |
| [9] | Tang Chang-bin;Liu Dao-xin;Wang Zhan;Gao Yang .Electro-spark alloying using graphite electrode on titanium alloy surface for biomedical applications[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2011(15):6364-6371. |
| [10] | Levashov EA;Vakaev PV;Zamulaeva EI;Kudryashov AE;Pogozhev YS;Shtansky DV;Voevodin AA;Sanz A .Nanoparticle dispersion-strengthened coatings and electrode materials for electrospark deposition[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2006(3):1161-1165. |
| [11] | Zamulaeva EI;Levashov EA;Kudryashov AE;Vakaev PV;Petrzhik MI .Electrospark coatings deposited onto an Armco iron substrate with nano- and microstructured WC-Co electrodes: Deposition process, structure, and properties[J].Surface & Coatings Technology,2008(15):3715-3722. |
| [12] | 王洪祥,张旭,高石,刘占山.1Cr13不锈钢电火花表面强化层摩擦磨损性能研究[J].材料科学与工艺,2011(03):56-59,65. |
| [13] | TANG Siu Kei .The Process fundamentals and parame-ters of electro-spark deposition[D].Waterloo,Ontario,Canada,2009. |
| [14] | 范林,李晓刚,杜翠薇,刘智勇.X80管线钢钝化膜在各种高浓度NaHCO3溶液中的电化学行为[J].中国腐蚀与防护学报,2012(04):322-326. |
| [15] | 贺俊光,文九巴,李旭东,郝庆国.Al-Zn-Sn-Ga阳极腐蚀过程的电化学阻抗谱[J].中国有色金属学报,2012(01):187-193. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%