利用电磁搅拌和固态挤压技术制备了Al-5％Fe-1．2％Si_1％Mg-O．6％Cu-o．5％Mn合金板坯，再经不同轧制工艺轧制成合金板，研究了其表面质量、显微组织及性能。结果表明：在温度为460℃、6道次、道次压下量为2mm工艺轧制的合金板表面质量最好；富铁相的破碎效果随道次压下量的增大而变好；采用温度为400℃、4道次、道次压下量为3mm工艺轧制的合金板富铁相形态最圆整，尺寸最小，其室温下的抗拉强度和伸长率最高，达到354．5MPa和7．6％，且在200～300℃热稳定性较好。
The alloy plate blanks of Al-5 %Fe-1.2 %Si-10% Mg-0. 6%Cu-0. 5% Mn prepared by electromagnetic stirring and solid extrusion we~Cre rolled by different rolling processes, and their surface quality, microstructure and properties were studied. The results show that the surface quality of the alloy sheet was best when the rolling temperature was 460 ℃ and reduction in six passes was 2 mm; the crushing effect of iron-rich phase became better with the increase of the pass reduction; the iron-rich phase of the alloy sheet with 400℃ rolling temperature and 3 mm reduction in four passes had best spherical shape and smallest size, and tensile strength at room temperature and elongation of thealloy sheet reached 354. 5 MPa and 7. 6% respectively, and its heat stability at 200--300 ℃ was better.
参考文献
| [1] | 谭敦强,黎文献,唐谊平.Al-Fe系合金中的相及相转变[J].材料导报,2003(05):18-20,27. |
| [2] | 杨江波.改善铝硅合金中铁相形态的措施[J].铸造,2000(08):454. |
| [3] | 周涛,黄伯云,周科朝,黎文献.快速凝固耐热铝合金耐蚀性能的研究[J].稀有金属材料与工程,2004(02):187-189. |
| [4] | 袁晓光,赵树国,李胜,卢云杰,黄宏军.半固态挤压Al-Si-Fe合金组织与性能[J].铸造,2006(05):466-468. |
| [5] | 张奎,刘国钧,张永忠,徐骏,吕晋宁,樊建中,张少明,石力开.半固态金属制备原理与应用[J].稀有金属,1998(06):447-449. |
| [6] | 宋毅飞 .半固态成形工艺对Al-5Fe合金组织和力学性能的影响[D].沈阳工业大学,2007. |
| [7] | 王建华 .2618耐热铝合金的组织与力学性能的研究[D].中南大学,2003. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%