A new method was developed by a thermal wear machine to evaluate the thermal wear of rolls in steel rolling process.The steel strip and rolls were simulated by upper and lower heating disks.The upper heating disk could be kept at a temperature of over 900℃ by induction heating.The pressure between the disks as high as 323.2 MPa could be achieved and the slipping rate could be 12.7%.The thermal wear of high speed steel(HSS)roll material,the wear rate of the HSS roll,and the SEM morphology of a worn HSS roll surface were investigated.This method was useful and could be employed to simulate friction and wear between strip and roll during the strip rolling process.
参考文献
| [1] | Kato Osamu .Mechanisms of Surface Deterioration of Roll for Hot Strip Rolling[J].ISU International,1992,32(11):1216. |
| [2] | GUO Xin-cheng;ZENG Qing-mei;sHU De-lin .Hot wear and Thermal Fatigue Properties of Several Roll Materials[J].Iron and Steel,1992,27(11):37. |
| [3] | 李志,曲敬信,周平安,赵振业,邵荷生.3Cr2W8V钢高温高载下的干摩擦滑动磨损特性[J].钢铁研究学报,2000(04):36-42. |
| [4] | LIAO Qian-chu;CUI Pei-yong .A Device for Simulating Study on Roll Wearing Process in Hot Rolling With In-Situ SEM Observation[J].Iron and Steel,1990,25(09):46. |
| [5] | LI Chang-sheng .Investigation on Characteristics of Rolls Surface in Hot Strip Mill[D].沈阳:东北大学出版社,2001. |
| [6] | Li C S;Xu J zZ;He X M et al.Formation and Control for Strip Scale Pores in Hot Rolling[J].Journal of Materials Processing Technology,2001,116(2-3):201. |
| [7] | C.S. Li;X.H. Liu;J.Z. Xu .FEM Analysis of Stress on Roll Surface Black Oxide Layers Exfoliation in Hot Strip Rolling[J].Journal of Materials Engineering and Performance,2002(2):215-219. |
| [8] | Lundburg;Sven-erik;Gustafsson .Influence of Rolling Temperature on Roll Wear,Investigated in a New High Temperature Test Rig[J].Journal of Materials Processing Technology,1994,42(05):239. |
| [9] | WANG Jiu-bin;LI Qing-ehun .Wearing Behavior of High Cr-Cast Iron Roll Caused by Rolling and Sliding Movement[J].Iron and Steel Research,1994,77(02):24. |
| [10] | GAO Cai-qiao .Friction Metallography[D].Harbin:Press of Harbin Institute of Technology,1988. |
| [11] | LUO Hong;Llu Jian-jun;ZHANG Zhi-jan .Sliding Abrasive Wear Characteristics of Steels with Different Hardness[J].Tribology,1994,14(03):213. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%