采用化学共沉淀法制备Sr4Al14O25∶Eu2+、Dy3+长余辉发光粉体.研究了H3BO3的加入对粉体的相组成,晶体结构,发光性能与长余辉特性的影响.结果表明,加入的H3BO3大部分不进入晶格,作为助熔剂有利于Sr4Al14O25相的形成,一小部分H3BO3进入晶格中取代Al3+离子并且对Sr4Al14O25∶Eu2+、Dy3+长余辉发光粉体的发光性能与长余辉特性都有显著的提高, 然而过量的H3BO3加入则会降低粉体的长余辉特性, 本实验所获得H3BO3合适的添加量为0.7mol.
参考文献
| [1] | Szigeti G.[A].Budapest Akademiai Kiado,1968:903. |
| [2] | Smets B;Rutten J;Hoeks G .[J].Journal of the Electrochemical Society,1989,136(07):2119. |
| [3] | Jia WY.;Lu LZ.;Liu HM.;Yen WM.;Yuan HB. .Phosphorescent dynamics in SrAl2O4 : Eu2+, Dy3+ single crystal fibers[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,1998(0):424-428. |
| [4] | Yamamoto H;Matsuzawa T .[J].Journal of Luminescence,1997,287:72-74. |
| [5] | Lin Y;Yang Z;Zhang Z .[J].Materials Letters,2001,51:14. |
| [6] | 宋庆梅,黄锦斐,吴茂钧,陈暨跃.铝酸锶铕的合成与发光的研究[J].发光学报,1991(02):144-150. |
| [7] | Rutten J;Hoeks G;Verlijsdonk J .[J].Journal of the Electrochemical Society,1989,136(07):2119-2123. |
| [8] | WANG M;Wang D;Lu G .[J].Materials Science and Engineering,1998,B57:18-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%