铂改性铝化物涂层的热生长层内应力研究

稀有金属材料与工程, 2011, 40(11): 1956-1960.

铂改性铝化物涂层的热生长层内应力研究

张德丰 ^1, , 陆建生 ^2, , 宋鹏 ^3, , 吕建国 ^4,

1.昆明理工大学,云南昆明650093

2.昆明理工大学,云南昆明650093

3.昆明理工大学,云南昆明650093;Forschungszentrum Juelich, IEF-2, Juelich 52425, Germany

4.昆明理工大学,云南昆明650093

关键词：铂改性铝化物 , 粘结层 , 氧化 , 内应力

TGO Stress Growth for Pt-Modified Aluminide Bond Coats during High Temperature Oxidation

研究了镍基高温合金热障涂层系统中铂改性铝化物粘结层在空气中非连续高温氧化生成的Al2O3层内应力状态及相应的粘结层微观结构.利用Raman光激发荧光谱技术,发现铂铝粘结层在900℃氧化初期生成了θ-和α-Al2O3,而在1100℃氧化时,表面则形成连续致密的α-Al2O3层.通过α-Al2O3的光激发荧光谱偏移量,计算得到了热障涂层中热生长层的内压应力略高于3.0 GPa.铂改性铝化物涂层表面Al2O3“背脊”处的内应力相对较低,同时由于没有陶瓷层的压制,生成的Al2O3起伏较大,并发生局部的Al2O3脱落.随氧化时间延长,由于Al元素沿晶界扩散较快,导致更多的γ′-Ni3Al在粘结层晶界处形成,粘结层中基本相β-NiAl向γ′-Ni3Al转变,改变了粘结层本身的热膨胀系数,引起热生长层中内应力变化.

参考文献

[1]	Nitin P P et al.[J].Science,2002,296:280.
[2]	Tolpygo VK;Clarke DR;Murphy KS .Evaluation of interface degradation during cyclic oxidation of EB-PVD thermal barrier coatings and correlation with TGO luminescence[J].Surface & Coatings Technology,2004(0):62-70.
[3]	Tolpygo V K et al.[J].Acta Materialia,2008,56:489.
[4]	Angenete J.;Stiller K.;Bakchinova E. .Microstructural and microchemical development of simple and Pt-modified aluminide diffusion coatings during long term oxidation at 1050 degrees C[J].Surface & Coatings Technology,2004(3):272-283.
[5]	Evans A G et al.[J].Progress in Materials Science,2001,46:505.
[6]	Qin F;Anderegg JW;Jenks CJ;Gleeson B;Sordelet DJ;Thiel PA .The effect of Pt on Ni3Al surface oxidation at low-pressures[J].Surface Science: A Journal Devoted to the Physics and Chemistry of Interfaces,2007(1):146-154.
[7]	Taylor MP;Evans HE;Busso EP;Qian ZQ .Creep properties of a Pt-aluminide coating[J].Acta materialia,2006(12):3241-3252.
[8]	Tolpygo V K et al.[J].Materials at High Temperatures,2000,17:59.
[9]	Warnes BM;Punola DC .Clean diffusion coatings by chemical vapor deposition[J].Surface & Coatings Technology,1997(1/3):1-6.
[10]	Nychka J A et al.[J].Surface and Coatings Technology,2001,146-147:110.
[11]	Selcuk A.;Atkinson A. .Analysis of the Cr3+ luminescence spectra from thermally grown oxide in thermal barrier coatings[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):147-156.
[12]	Wang Y et al.[J].Acta Materialia,2004,52:2665.
[13]	Zhao J C .[J].Advances in Engineering Materials,2001,3:143.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网