设计了系列成分的Al-Mg-Zn三元合金，采用大气造渣保护熔炼技术制备了Al-Mg-Zn合金铸锭，进行了电化学性能测试和阳极保护试验，建立了ALMg-Zn三元合金自腐蚀电位一成分图。发现Al，MgyZn1-x-y合金当32-0．2～0．6，y=0～0．4时，具有较低的自腐蚀电位和自腐蚀电流密度，分别为-1．03～-1．25V（vs．SCE）和8．7×10^-7-5．01×10^-5A／cm^2；同时，Al0.2Mg0.2 Zno6和Al0.6 Mg0.2 Zn0.2合金在3．5％NaCl溶液中对Q235钢具有良好的保护作用。
A series of Al-Mg-Zn alloys were prepared by flux melting in the atmosphere. The as-prepared alloys were investigated by electrochemical performance testing and anodic protection experiment. Al-Mg-Zn electrode potential-component ternary plot was established. The results show that when x and y were equal to 0.2-0. 6 and 0-0.4 respectively, the corrosion current density and free corrosion potential of alloys were very low, Ecorr was between -1.03 Vand -1.25 V（vs. SCE）, Jcorr was between 8. 7×10^-7 A/cm^2 and 5. 01×10^-5 A/cm^2. At the same time, Al0. 2 Mg0. 2 Zn0. 6 and Al0. 6 Mg0. 2 Zno. 2 alloys had a good protective effect for Q235 steel in the solution of 3.50% NaCl.
参考文献
| [1] | Sonatrach MB.;Salhi E.;Sonatrach KB.;Ghali E.;Lepmi FD. .A comparative study of the electrochemical behaviour of Algerian zinc and a zinc from a commercial sacrificial anode[J].Journal of Materials Science,2003(6):1139-1145. |
| [2] | Waheed A. Badawy;Nadia H. Hilal;Mohmmed El-Rabiee;H. Nady .Electrochemical behavior of Mg and some Mg alloys in aqueous solutions of different pH[J].Electrochimica Acta,2010(6):1880-1887. |
| [3] | 左列 .大功率动力电池用铝合金阳极材料研究[D].中南大学,2009. |
| [4] | 齐公台,郭稚弧,林汉同,魏伯康.腐蚀保护常用的几种牺牲阳极材料[J].材料开发与应用,2001(01):36-40. |
| [5] | 潘应君,张恒,黄宁,高松超,徐峰.热喷涂Zn-15%Al合金的耐蚀性研究[J].腐蚀与防护,2002(12):526-528. |
| [6] | 潘应君,张恒,黄宁,高松超,徐峰.Zn-Al合金在长江水中的耐蚀性研究[J].腐蚀科学与防护技术,2003(04):231-233. |
| [7] | 从善海,侯强.环氧富Zn-Al-Mg-Ce合金涂层耐腐蚀性能[J].中国表面工程,2010(01):57-62,68. |
| [8] | R. Udhayan;Devendra Prakash Bhatt .On the corrosion behaviour of magnesium and its alloys using electrochemical techniques[J].Journal of Power Sources,1996(1):103-107. |
| [9] | Waheed A. Badawy;Nadia H. Hilal;Mohmmed El-Rabiee;H. Nady .Electrochemical behavior of Mg and some Mg alloys in aqueous solutions of different pH[J].Electrochimica Acta,2010(6):1880-1887. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%