以甘氨酸作燃烧剂采用燃烧法制备Y_2Zr_2O_7:Tb~(3+)纳米晶粉末.用X射线衍射仪(XRD)、高分辨透射电子显微镜(HRTEM)和荧光分光光度计对Y_2Zr_2O_7:Tb~(3+)纳米晶的相结构、形貌和发光性质进行研究.结果表明:所得到的纳米晶粒度均匀、结晶完好,属于立方萤石结构.发光光谱的测试表明:Tb~(3+)呈现其特征绿色发射,最强峰位于542 nm处.Tb~(3+)的掺杂摩尔浓度在0.5%～6%的范围内,3%为最佳掺杂浓度.
Y_2Zr_2O_7:Tb~(3+) nano-phosphors were fabricated by combustion synthesis method using glycine as incendiary agent. X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM) and fluorescence spectrometer were used to characterize the phase structure, surface morphology and luminescence property of Y_2Zr_2O_7:Tb~(3+) nano-phosphors. The results show that the prepared samples have uniform crystallinity and fine crystalline, with a cubic fluorite structure. Typical Tb~(3+) emission peaks were observed in the fluorescence spectra and the strongest emission at about 542 nm with green color corresponded to the ~5D_4→~7F_5 transition. The doping concentration of Tb~(3+) was in the range of 0.5%-6%, with the optimum of 3%.
参考文献
| [1] | Dhas N A;Patil K C .[J].Journal of Materials Chemistry,1993,3(12):1289. |
| [2] | 徐美;张慰萍;江寅 et al.[J].发光学报,2005,26(05):582. |
| [3] | 林崔昆,于敏,逄茂林,林君.溶胶-凝胶法合成（Ce, Tb）GdMgB5O10及其发光性质的研究[J].中国稀土学报,2005(03):266-270. |
| [4] | 石士考,王继业.甘氨酸燃烧合成YAG：Tb荧光粉的微观结构和发光特性[J].无机化学学报,2002(04):431-434. |
| [5] | 张茂峰,孟建新,刘应亮,满石清.水热法制备LaF3：Ce,Tb纳米荧光粉及发光性质研究[J].光谱学与光谱分析,2007(02):232-235. |
| [6] | 于立新,宋宏伟,刘钟馨,杨林梅,吕少哲,郑著宏.LaPO4：Ce3+/Tb3+ 纳米线的合成和发光特性[J].发光学报,2005(03):369-374. |
| [7] | 韩秀梅,林君,李哲,齐西伟,李明亚,王晓强.Ca2Gd8（SiO4）6O2：Tb3+薄膜的制备及其发光性能研究[J].稀有金属材料与工程,2007(z1):866-868. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%