本文采用挤压铸造的方法制备了7075铝合金传动空心轴,研究了Al-5Ti-B及RE对挤压铸造7075铝合金铸件微观组织和力学性能的影响.结果表明:未加入细化剂的合金晶粒大小约为50μm,拉伸强度为454 MPa;加入0.29%RE的合金和1%A1-5Ti-B的合金,晶粒尺寸分别了减小到26μm和25μm,拉伸强度分别提高了16.3%和22.2%;同时加入0.29%RE和1%A1-5Ti-B对合金组织细化最为明显,晶粒尺寸减小到18μm,拉伸强度提高了26.6%,达到575MPa,延伸率为8.16%,布氏硬度为184.

The scaled pieces of 7075 Aluminum alloy hollow axle of transmission shaft was prepared by squeeze casting process.Study on effect of Al-5Ti-B and RE on microstructure and mechanical properties of 7075 Aluminum alloy.The results show that the grain size of alloy without refinement is about 50μm,Ten-sile strength is 454MPa;The grain size of the alloy with 0.29% RE and 1% Al-5Ti-B reduces to 26μm and 25μm.Tensile strength increases by 16.3% and 22.2%;Ddding 1% Al-5Ti-B and 0.29% RE in the alloy at the same time can reform microstructure mostly.The grain size of alloy reduces to 18μm,The tensile strength increases by 26.6% and comes to 575MPa,Elongation percentage is 8.16% and brinell hardness is 184.

参考文献

[1] 郭国文 .高强韧铸造铝合金材料及其挤压铸造技术的研究[D].华南理工大学,2002.
[2] 鲁春艳.汽车轻量化技术的发展现状及其实施途径[J].轻型汽车技术,2007(06):22-25.
[3] 刘岩.我国高速铁路客车轻量化车体最优结构研究[J].轻合金加工技术,2000(05):41-43.
[4] 张永安,熊柏青,朱宝宏,刘红伟,石力开,王洪斌,张济山.Al10Zn2.9Mg1.7Cu超高强铝合金的喷射成形制备研究[J].稀有金属,2003(05):609-613.
[5] 庞磊,张兴国,郝海,房灿峰,李昕,金俊泽.7050铝合金晶粒细化的研究[J].特种铸造及有色合金,2007(06):479-481.
[6] 刘红卫,陈康华.原位合成TiB2和Al3Ti对ZL201的晶粒细化效果[J].特种铸造及有色合金,2000(02):4-6.
[7] 樊刚,程钢.稀土金属在铸造铝合金中的应用[J].昆明理工大学学报,2002(02):13-16.
[8] 胥锴,刘政,刘萍.稀土在铝及铝合金中的应用现状与展望[J].有色金属加工,2005(05):10-14,36.
[9] 水丽,孙伟成.AlTiB和AlTiBRe对铝合金晶粒细化的影响[J].新技术新工艺,2003(05):42-43.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%