采用脉冲激光沉积技术在Si(100)衬底上制备了高导电的IrO2薄膜,重点研究了退火前后其电学性能和微观结构的变化规律.采用X射线衍射(XRD)、原子力显微镜(AFM)、光电子能谱(XPS)和四探针法对退火前后IrO2薄膜的结构和电性能进行了表征,并利用霍尔效应研究了IrO2薄膜的导电机理.结果表明:IrO2薄膜在空气中退火后,导电性能得到提高,其中在750℃退火的电阻率达到最小值37μΩ·cm.在25～500℃范围内,IrO2薄膜的高温电阻率随着温度的升高呈线性关系逐渐增大,呈现出类似金属的导电特征.在250～400℃沉积的IrO2薄膜载流子的类型为p型；沉积温度较高(500℃)或在更高温度退火处理后,IrO2薄膜载流子的类型为n型,其导电机理以电子导电为主.
参考文献
| [1] | Fierro, S;Kapalka, A;Frey, O;Koudelka, M;Comninellis, C .Microelectrode-array of IrO2 prepared by thermal treatment of pure Ir[J].Electrochemistry communications,2010(4):587-591. |
| [2] | Backholm J;Avendano E;Azens A;de M Azevedo G;Coronel E;Niklasson GA;Granqvista CG .Iridium-based oxides: Recent advances in coloration mechanism, structural and morphological characterization[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2008(2):91-96. |
| [3] | Korotcov A;Hsu H P;Huang Y S et al.[J].Journal of Raman Spectroscopy,2006,37(12):1411. |
| [4] | 王世军,丁爱丽,仇萍荪,何夕云,罗维根.直流磁控反应溅射制备IrO2薄膜[J].无机材料学报,2000(04):733-739. |
| [5] | Slavcheva E;Radev I;Bliznakov S et al.[J].Electrochimica Acta,2007,52(12):3889. |
| [6] | Thanawala S;Georgiev D G;Baird R J et al.[J].THIN SOLID FILMS,2007,515(18):7059. |
| [7] | Liu Y X;Masumoto H;Goto T .[J].Materials Transactions,2004,45(10):3023. |
| [8] | Elkhakani M A;Chaker M .[J].THIN SOLID FILMS,1998,335(1-2):6. |
| [9] | Patil PS.;Chigare PS.;Sadale SB.;Seth T.;Amalnerkar DP.;Kawar RK. .Thickness-dependent properties of sprayed iridium oxide thin films[J].Materials Chemistry and Physics,2003(3):667-675. |
| [10] | Nishio K;Watanabe Y;Tsuchiya T .[J].THIN SOLID FILMS,1999,350(1-2):96. |
| [11] | Gong Y S;Wang C B;Shen Q et al.[J].Materials Chemistry and Physics,2009,116:573. |
| [12] | Chen T S;Balu V;Jiang B et al.[J].lntegratedFerroelectrics,1997,17:191. |
| [13] | Lee H S;Um W S;Hwang K T et al.[J].Journal of Vacuum Science and Technology A:Vacuum Surfaces and Films,1999,17:2939. |
| [14] | 夏明祥,王传彬,公衍生,沈强,张联盟.脉冲激光沉积技术制备IrO2薄膜的研究[J].稀有金属材料与工程,2006(05):820-823. |
| [15] | Zhang LM;Gong YS;Wang CB;Shen Q;Xia MX .Substrate temperature dependent morphology and resistivity of pulsed laser deposited iridium oxide thin films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2006(2):371-375. |
| [16] | 张玉勤,董显平,吴建生.（Cr-Si-Ni）/Si薄膜的微观结构和电阻率[J].中国有色金属学报,2005(05):746-750. |
| [17] | Neugebauer C A;Webb M B .[J].Journal of Applied Physics,1962,33(01):74. |
| [18] | Wu F;Mclaurin A W;Henson K E et al.[J].THIN SOLID FILMS,1998,332(1-2):418. |
| [19] | Wu F;Morris J E .[J].THIN SOLID FILMS,1994,246(1-2):17. |
| [20] | 陈东初 .[D].武汉:华中科技大学,2004. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%