研究了烧结工艺对粉末注射成胗4J32低膨胀合金性能的影响.结果表明,提高烧结温度或延长保温时间均能提高合金的致密度,但也会使其晶粒长大;而在氢气或高真空气氛下烧结能获得更好的性能.在最佳烧结工艺下,即烧结温度1350℃、烧结时间120 min及氢气气氛,获得了高性能的PIM 4J32低膨胀合金,其致密度为98.3%,在低于100℃的温度范围内,平均膨胀系数仅为0.3×10-6K-1,优于传统方法制备的合金性能及国家相应标准.该合金组织由奥氏体γ主体相及极少量的马氏体α相组成.
参考文献
| [1] | 刑绍美.[J].航天工艺,1998(06):34. |
| [2] | Huang F Y;Chow H M;Chen S L et al.[J].Journal of Materials Processing Technology,1999,87(1-3):112. |
| [3] | Suri P.;Atre SV.;German RM.;de Souza JP. .Effect of mixing on the rheology and particle characteristics of tungsten-based powder injection molding feedstock[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):337-344. |
| [4] | 段柏华,曲选辉,邹黎明,郭世柏,秦明礼.注射成形法制取各向异性粘结NdFeB磁体的研究[J].稀有金属材料与工程,2005(08):1251-1254. |
| [5] | Eroglu S;Bakan H I .[J].Powder Metallurgy,2005,48(04):329. |
| [6] | Qu X H;Gao J X;Qin M L et al.[J].International Journal of Refractory Metals & Hard Materials,2005,23(4-6):273. |
| [7] | Simmons K;Scott W K;Nyberg E et al.[J].Industrial Heating,2005,72(12):43. |
| [8] | 段柏华,周晓晖,曲选辉,徐征宙.Kovar合金注射成形工艺研究[J].矿冶工程,2004(05):70-72. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%