提出一种用以解决连铸板坯角横裂纹缺陷的倒角结晶器技术。倒角结晶器的数值仿真和工业化试验表明：倒角铸坯在连铸矫直区角部温度可以提高70℃以上,能够避开钢的高温低塑性区;同时,倒角的特殊的结构形式可以降低铸坯角部的Z向应力,有助于控制角横裂纹缺陷。
A chamfering mold technology was brought forward to remove the transverse corner crack of continuous casting slab.Numerical simulation and industrial experiment of chamfering mold show that the corner temperature of chamfered slab can be increased more than 70 ℃ at straightening section,which escape the high temperature inductile zone of steel.At the same time,the structure of bevel edge can decrease the Z-direction stress of continuous casting slab to control the transverse corner crack.
参考文献
| [1] | Mintz B;Yue S;Jonas J J .Hot Ductility of Steelsand Its Re- lationship to the Problem of Transverse Cracking During Con tinuous Casting[J].International Materials Reviews,1991,36(05):187. |
| [2] | 张洪波;王海之 .结晶器振动参数与保护渣物化性能的相互关系[J].钢铁,1995,30(11):19. |
| [3] | Coleman T H J;Wilcox R .Transverse Cracking in Continu- ously Cast HSLA Slabs-Influence of Composition[J].Materi- als Science and Technology,1985,1(01):80. |
| [4] | Hannerz N E.Critical Hot Plasticity and Transverse Cracking in Continuous Slab Casting With Particular Reference of Com- position[J].Transactions of the Iron and Steel Institute of Japan,1985(25):149. |
| [5] | Crowther D N;Green M J W;Miehell P S.Microalloying in Steel[M].Switzerland:Trans Tecb Publications Ltd,1998 |
| [6] | 蔡开科.连铸技术的进展（一）[J].炼钢,2001(01):7-12. |
| [7] | 刘新字 .微合金化钢铸坯碳氮化物的析出及高温延塑性的研究[D].北京:北京科技大学,2000. |
| [8] | 王新华,王文军,刘新宇,费惠春,张立,叶锦渭.减少含铌、钒、钛微合金化钢连铸板坯角横裂纹的研究[J].钢铁,1998(01):22-25. |
| [9] | Mintz B;Arrowsmith J M.Hot-Ductility Behavior of C Mn- Nb-AI Steels and Its Relationship to Crack Propagation Dur- ing the Straightening of Continuously Cast Strand[J].Metals and Technology,1979(01):24. |
| [10] | Hans-Jurgen, Klingelhofer;Klingelhofer G.Hydraulic Oscillation Drive for Resonance Molds[A].Pohang:Union Steel MFG Co,Ltd,1996:287. |
| [11] | Mintz B;Abushosha R.Influence of Vanadium on Hot Duc- tility of Steel[J].Ironmaking and Steelmaking,1993(20):445. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%