Four alloys TMS-75 (Base), Base+B, Base+C and TMD-103 (Base+B+C) with varying levels of B, C were directionally solidified (DS), and their weldability was investigated by bead-onplate electron beam welding. It was found that cracking occurred in the weld-metal, as well as in the heat affected zone (HAZ). Both γ/γ' and/or γ/carbide eutectic contributed to the weld-metal cracking, and theγ/γ' eutectic was found to be mainly responsible for cracking in HAZ. However, constitutional liquation of carbides seems to have made some contribution also.The B addition had a detrimental effect on HAZ cracking susceptibility, while C addition improved it appreciably even in the presence of B. In addition, no obvious differences were observed in cracking susceptibility of weld-metal in the four alloys. The cracking modes and mechanisms underlying the effect of B and C addition on weidability could be explained on the basis of microstructures of the four alloys.

参考文献

[1]
[2]
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%