Mg2Si reinforced Mg-Al based composite with high amount of silicon was prepared by permanent mould casting, and then extruded by reciprocating extension (RE) after the composite was processed by homogenization heat treatment. The effect of RE processing on the morphology and size of Mg2Si and the mechanical properties of the composite were investigated, to develop new ways to refine the Mg2Si phase and improve its shape. The result showed that RE was very useful in refining the Mg2Si phase.The more the RE processing passes, the better the refining effect would be. Moreover,the uniform distribution of Mg2Si phases would be more in the composite. After the composite was processed by RE for 12 passes, most Mg2Si phases were equiaxed, with granular diameter below 20 μm, and distributed uniformly in the matrix of the composite. The mechanical properties of the composite could be increased prominently by RE processing, and were much higher than that in the as-cast state. As the temperature rises, the tensile strength is reduced. For the composite RE processed for 12 passes, the tensile strength, yield strength, and elongation are 325.9 MPa, 211.4 MPa,and 3.3% at room temperature, whereas, 288.2 MPa, 207.7 MPa, and 7.8%, respectively, at 150° C. In comparison with the properties at room temperature, the tensile strength and yield strength are high and only decrease by 11.6% and 1.8% at 150°C. The Mg2Si reinforced Mg-Al based composite possesses good heat resistance at 150° C. The excellent resistance to effect of heat is attributed to the high melting temperature and good thermal stability of fine Mg2Si phases, which are distributed uniformly in the composite, and effectively hinder the grain boundary gliding and dislocation movement.
参考文献
| [1] | E Aghion;B Bronfin .[J].Materials Science Forum,2000,350-351:19. |
| [2] | B L Mordike;T Ebert .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2001,302:37. |
| [3] | J. Zhang;Z. Fan;Y. Q. Wang;B. L. Zhou .Microstructural development of Al-15wt.%Mg{sub}2Si in situ composite with mischmetal addition[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):104-112. |
| [4] | B. Bronfin;M. Katsir;E. Aghion .Preparation and solidification features of AS21 magnesium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1):46-50. |
| [5] | G Y Yuan;M P Liu;W J Ding;A.Inoue .[J].Materials Science Forum,2003,419-422:425. |
| [6] | M Mabuchi;K Kubota;K Higashi .[J].Journal of Materials Science,1996,31:1529. |
| [7] | Y Z Lü;Q D Wang;X Q Zeng;Y P Zhu and W J Ding .[J].Materials Science and Engineering,2001,A301:255. |
| [8] | M.S. DARGUSCH;A.L. BOWLES;K. PETTERSEN .The Effect of Silicon Content on the Microstructure and Creep Behavior in Die-Cast Magnesium AS Alloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2004(6):1905-1909. |
| [9] | M. MABUCHI;K. HIGASHI .STRENGTHENING MECHANISMS OF Mg-Si ALLOYS[J].Acta materialia,1996(11):4611-4618. |
| [10] | M. Richert;H. P. Stuwe;M. J. Zehetbauer .Work hardening and microstructure of AlMg5 after severe plastic deformation by cyclic extrusion and compression[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):180-185. |
| [11] | M Richert;J Richert;J Zasadzinski;S.Hawrylkiewicz and J.Dlugopolski .[J].Materials Chemistry and Physics,2003,81:528. |
| [12] | W L Lu;Y Wang;Z Z Feng;J T Hai.[J].HotWorking Technology,2001(02):10. |
| [13] | S.-W. Lee;J.-W. Yeh;Y.-S. Liao .Premium 7075 Aluminium Alloys Produced by Reciprocating Extrusion[J].Advanced Engineering Materials,2004(12):936-943. |
| [14] | S Y Yuan;J W Yeh;C H Tsau .[J].Materials Transactions-Japan Institute of Metals,1999,40:233. |
| [15] | J W Yeh;S Y Yuan;C H Peng .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1998,252:212. |
| [16] | C F Li;J Wang;K Li;D Shu,B D Sun .[J].The Chinese Journal of Nonferrous Metals,2004,14:233. |
| [17] | G Y Yuan;M P Liu;Q D Wang;Y P Zhu and W J Ding .[J].Aeta Metall Sin,2002,38:1105. |
| [18] | S K Guan;Y X Wang.[J].Auto Technol Mater,2003(04):3. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%