以连续介质损伤力学(CDM)为基础,提出了一个有效的数值分析模型来模拟碳纤维增强复合材料(CFRP)层合板低速冲击的接触力响应和能量响应.该模型考虑了不同的失效模式,引入了不可逆的损伤变量和新的刚度折减方式以考虑损伤造成的刚度变化,定义了耗散能的计算方式以考虑损伤造成的能量变化.通过在Abaqus/Explicit平台上编写VUMAT子程序具体实现模型,数值仿真与试验结果吻合较好,验证了该模型的有效性.此外,还综合考虑了Hashin准则与LaRC04准则各自的优缺点,用Hashin和LaRC04相混合得到的准则对低速冲击进行了模拟.结果表明:在冲击外载作用下当CFRP层合板中存在较多基体压缩失效时,采用混合的失效准则模拟得到的接触力响应和能量响应结果更接近试验结果,而使用纯Hashin准则得到的预测结果偏保守.
参考文献
[1] | Meo M;Morris A J;Vignjevic R.Numerical simula tions of low-velocity impact on an aircraft sandwich panel[J].Computers & Structures,200362(3):353-360. |
[2] | J.P.Hou;N.Petrinic;C.Ruiz;S.R.Hallett.Prediction of Impact Damage in Composite Plates[J].Composites science and technology,20002(2):273-281. |
[3] | Prediction of impact-induced delamination in cross-ply composite laminates using cohesive interface elements[J].Composites science and technology,200812(12):p.2383. |
[4] | Zou Z;Reid S R;Li S.Application of a delamination model to laminated composite structures[J].Computers & Structures,200256(4):375-389. |
[5] | 张彦;朱平;来新民;梁新华.低速冲击作用下碳纤维复合材料铺层板的损伤分析[J].复合材料学报,2006(2):150-157. |
[6] | M.V. Donadon;L. Iannucci;B.G. Falzon;J.M. Hodgkinson;S.F.M. de Almeida.A progressive failure model for composite laminates subjected to low velocity impact damage[J].Computers & structures,200811/12(11/12):1232-1252. |
[7] | 毛春见;许希武;田静;徐焜.缝合复合材料层板低速冲击损伤研究[J].固体力学学报,2011(1):43-56. |
[8] | SystèmesD.Abaqus analysis user's manual[M].,2010 |
[9] | 沈真;张子龙;王进;杨胜春;叶林.复合材料损伤阻抗和损伤容限的性能表征[J].复合材料学报,2004(5):140-145. |
[10] | Pinho S T;Dàvila C G;Camanho P P et al.Failure models and criteria for FRP under in-plane or three-dimensional stress states including shear non-linearity,NASA/TM 2005-213530[R].Hanpton,VA:NASA Langley Research Center,2005. |
[11] | Hashin Z;Rotem A.A fatigue failure criterion for fiber reinforced materials[J].Journal of Composite Materials,19737(4):448-464. |
[12] | Hashin Z .Fatigue failure criteria for unidirectional fiber composites[R].Pennsylvania:Philadelphia Department of Materials Science and Engineering,Pennsylvanina State Vinversity,1980. |
[13] | Ireneusz Lapczyk;Juan A. Hurtado.Progressive damage modeling in fiber-reinforced materials[J].Composites, Part A. Applied science and manufacturing,200711(11):2333-2341. |
[14] | A. Matzenmiller;J. Lubliner;R.L. Taylor.A constitutive model for anisotropic damage in fiber-composites[J].Mechanics of materials,19952(2):125-152. |
[15] | Wang Y;Tong M;Zhu S.Three dimensional continuum damage mechanics model of progressive failure analysis in fibre-reinforced composite laminates[A].California:American Institute of Aeronautics and Astronautics,2009 |
[16] | C.F. Li;N. Hu;Y.J. Yin.Low-velocity impact-induced damage of continuous fiber-reinforced composite laminates. Part I. An FEM numerical model[J].Composites, Part A. Applied science and manufacturing,20028(8):1055-1062. |
[17] | Camanho P P.Advances in the simulation of damage and fracture of composite structures[A].Pamplona,2005 |
[18] | J.R. Xiao;B.A. Gama;J.W. Gillespie Jr..Progressive damage and delamination in plain weave S-2 glass/SC-15 composites under quasi-static punch-shear loading[J].Composite structures,20072(2):182-196. |
[19] | CYCTC Engineered Materials Inc.Mechanical properties of CYCOM(R) 977-2-35%-12KHTS-134[M].Arizona United States:Cytec Engineered Materials Inc,2010 |
[20] | Systèmes D .Analysis of composite materials with Abaqus[OL].http:// ishare.iask.sina.com.cn/f/17040149,2013-09-03. |
[21] | D7136/D7136M-05 Standard test method for measuring the damage resistance of a fiber-reinforced polymer matrix composite to a dropweight impact event[S].West Conshohocken (PA):ASTM International,2005. |
[22] | Systèmes D.Abaqus user subroutines reference manual[M].,2010 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%