通过机械球磨的方法成功制得Mg55Ni35Si10非晶粉末,并采用X射线衍射(XRD)对其非晶形成过程进行研究,发现Mg55Ni35Si10粉末样品在球料比为20:1、转速为600r/min的条件下,经过54h球磨后开始形成完全的非晶结构.还采用差示扫描量热仪(DSC)对Mg55Ni35Si10非晶粉末的热稳定性进行了研究,通过Kissinger方程得到样品开始晶化的表观激活能为(280.6±44.5)kJ/mol,与文献中报道的Mg65Cu25Gd10的激活能((285.2±27.6)kJ/mol)相近,说明样品具有较好的热稳定性.此外,还对Mg55Ni35Si10非晶在NaCl溶液中的腐蚀行为进行了研究,发现该样品的腐蚀电位远远正于AZ31和AZ61镁合金,表明Mg55Ni35Si10非晶具有较好的耐腐蚀性能.
参考文献
| [1] | 陈振华.镁合金[M].北京:化学工业出版社,2004 |
| [2] | Baricco M;Castellero A;Chio M Di et al.Thermal stability and hardness of Mg-Cu-Au-Y amorphous alloys[J].Journal of Alloys and Compounds,2007,434:183. |
| [3] | Inoue A;Nishiyama N;Matsuda T .Preparation of bulk glassy Pd40 Ni10 Cu30 P20 alloy of 40mm in diameter by water quenching[J].Materials Transactions-Japan Institute of Metals,1996,37:181. |
| [4] | Hui X et al.Formation,microstructure and properties of long-period order structure reinforced Mg-based bulk metallic glass composites[J].Acta Materialia,2007,55:907. |
| [5] | Zhang T;Inoue A .Preparation of Ti-Cu-Ni-Si-B amorphous alloys with a large supercooled liquid region[J].Materials Transactions-Japan Institute of Metals,1999,40:301. |
| [6] | Gebert A;Haehnel V;Park E S .Corrosion behavior of Mg65Cu7.5Ni7.5Ag5Zn5Gd5Y5 bulk metallic glass in aqueous environments[J].Electrochimica Acta,2008,53:3403. |
| [7] | Qin F X et al.Corrosion behavior of the Mg55Cu25Gd10 bulk amorphous alloys[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,449:636. |
| [8] | TAN Chao-Gui,JIANG Wen-juan,WU Xue-qing,WANG Xiu-feng,LIN Jian-guo.Effect of crystallization on corrosion resistance of Cu52.5Ti30Zrl 1.5Ni6 bulk amorphous alloy[J].中国有色金属学会会刊（英文版）,2007(04):751-754. |
| [9] | Lee P Y;Liu W C;Lin C K et al.Fabrication of Mg-Y-Cu bulk metallic glass by mechanical alloying and hot consolidation[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,449:1095. |
| [10] | Li Z G;Hui X;Zhang C M et al.Formation of Mg-Cu-Zn-Y bulk metallic glasses with compressive strength over gigapascal[J].Journal of Alloys and Compounds,2008,454:168. |
| [11] | Zhang ZF;Zhang H;Shen BL;Inoue A;Eckert J .Shear fracture and fragmentation mechanisms of bulk metallic glasses[J].Philosophical Magazine Letters,2006(10):643-650. |
| [12] | Gun B;Laws KJ;Ferry M .Superplastic flow of a Mg-based bulk metallic glass in the supercooled liquid region[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2006(36/37):3896-3902. |
| [13] | Ma H;Shi LL;Xu J;Li Y;Ma E .Discovering inch-diameter metallic glasses in three-dimensional composition space[J].Applied physics letters,2005(18):1915-1-1915-3-0. |
| [14] | Pan D G;Liu W Y;Zhang H F et al.Mg-Cu-Ag-Gd-Ni bulk metallic glass with high mechanical strength[J].Journal of Alloys and Compounds,2007,438:142. |
| [15] | Takagi M et al.Effect of preparation technique and atmosphere on the mechanical properties of bulk amorphous alloy compacts[J].Materials Science and Engineering,1991,A133:301. |
| [16] | Kissinger H E .Variation of peak temperature with heating rate in differential thermal analysis[J].Journal of Research of the National Bureau of Standards,1956,57(01):217. |
| [17] | Oleszak D;Kulik T .Ni59Zr20Ti16Sn5 amorphous alloy obtained by melt spinning and mechanical alloying[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2007(8/10):845-847. |
| [18] | XU Chun-xia,PAN Fu-sheng,WANG Jing-feng,TANG Ai-tao,HU Yao-bo.Synthesis of Mg-Cu-Gd amorphous alloy by mechanical alloying and its thermal stability[J].中国有色金属学会会刊（英文版）,2006(z3):1848-1850. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%