采用自制球磨机机械合金化Ti/Al二元粉 末， 研究了机械合金化过程中粉末结构的变化。 结果表明： Ti50Al50 混合粉 经高能球磨后， 颗粒尺寸迅速增大， 而后快速下降， Ti， Al晶粒各自逐渐细化至纳米尺 寸； 进一步球磨 ， 颗 粒尺寸减小甚微； 晶粒尺寸进一步细化导致形成非晶， 但在此过程中并没有发现Ti-Al金 属 间化合物的形成； 随球磨时间的延长， 粉末显微硬度开始略有下降， 然后迅速增加 ， 在基本形成非晶后， 保持恒定值。
The changes of powder microstructures of Ti/Al binary powder during mechanical alloying were investigated. The results showed that the granular size of composite po wders rapidly increases at first， and then promptly decreases， and gradually to magnitude of nanometer. After further milling, the amorphous material is for med due to grain minimizing. In the whole pro ce ss, no Ti-Al intermetallic compound was found to come into being. Wi th the milling time increasing, the microhardness decreases a little at first， and then rapidly increases， in the end it keeps a constant when amorphous microstructure is basically forme d.
参考文献
| [1] | Wang Wego.Aluminum alloys for aircraft applications[J].Journal of The Minerals,Metals & Materials Society,1993(09):16-18. |
| [2] | London B;Larsen D L Jr;Wheeler D A.Structural Intermetal lics[C].TMS,1993:151. |
| [3] | Ashida Y .Manufacturing process of TiAl sheets[J].Light Metals(in Japanese),1994,44(11):604-608. |
| [4] | Takeshi Kawabata;Hideaki fukai;Osamu izumi .Effect of ternary additions on mechanical properties of TiAl[J].Acta materialia,1998(6):2185-2194. |
| [5] | 张荻,覃继宁,施幸华.热轧态TiAl基金属间化合物超塑性变形的组织研究[J].稀有金属材料与工程,1998(04):210-214. |
| [6] | J.N.WANG .THE ROLE OF LEDGES IN CREEP OF TiAl ALLOYS WITH FINE LAMELLARSTRUCTURES[J].Acta materialia,1998(6):0-0. |
| [7] | Wang G X .An overview:TiAl-based alloys prepared by elemental pow der metallurgy[J].Powder Metallurgy,1992,24(04):219-225. |
| [8] | Doydhak J.Metal and intermetallic-matrix composites for aerospace prop ulsion and power systems[J].Journal of The Minerals,Metals & Materials Society,1992(06):4651. |
| [9] | Semiatin S L .Plastic-flow behavior and microstructural developme nt in a ca st alpha-two titanium aluminide[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,23(01):295. |
| [10] | S. Heshmati-Manesh;H. M. Flower .Microstructural evolution in silicon alloyed γ-Ti-Al alloys after thermomechanical processing[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1999(2):144-150. |
| [11] | 范雄.金属X射线学[M].北京:机械工业出版社,1988:103-122. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%