在真空环境下，将铜熔渗到钼纤维预制体中，制得纤维结构的致密的钼铜复合材料。通过控制钼纤维预制体的表观密度，可以方便地改变钼铜复合材料的成分组成。采用扫描电镜和金相显微镜观察材料的微观组织形貌，研究工艺参数对钼铜复合材料的成分、密度、硬度和电导率的影响。结果表明：采用无纺技术结合模压成形获得的钼纤维预制体可形成较宽范围的孔隙度，从而得到钼含量不同的钼铜复合材料；熔渗工艺制得的钼铜复合材料具有致密均匀、特征明显的纤维结构组织；所得钼铜复合材料的致密度均达到99%以上。当钼质量分数为84.77%时，得到的材料致密度达到最大值99.43%，其硬度为226.7HV，电导率为16.5 MS/m。
In vacuum environment, the dense fiber-structured molybdenum-copper (Mo-Cu) composites were fabricated by infiltrating liquid copper into molybdenum fibrous preform. By controlling the relative density of molybdenum fibrous preform, the composition of Mo-Cu composites could be easily changed. The microstructure and morphologies of Mo-Cu composites were observed by scanning electron microscopy and optical microscopy, and the effects of process parameters on the composition, physical and mechanical properties were investigated. The results indicate that molybdenum fibrous preform obtained by non-woven technology with mould pressing formation has wider range of porosity, Mo-Cu composite with different molybdenum contents are obtained. The Mo-Cu composites have dense and homogeneous structure with obvious fibrous character by infiltration. The relative density of the composites is above 99%. When the mass fraction of molybdenum is 84.77%, the maximum relative density reaches 99.43% for fiber-structured Mo-Cu composites. Meanwhile, their hardness and electrical conductivity are 226.7HV and 16.5 MS/m, respectively.
参考文献
| [1] | GUO Shibo,KANG Qiping,CAI Chunbo,Qu Xuanhui.Mechanical properties and expansion coefficient of Mo-Cu composites with different Ni contents[J].稀有金属（英文版）,2012(04):368-371. |
| [2] | 李在元,翟玉春.氢还原法制备Mo60Cu40纳米复合粉[J].稀有金属材料与工程,2010(01):6-9. |
| [3] | SUN Ao-kui;WANG De-zhi;WU Zhuang-zhi;CHENG Qi-jun .Mechanochemical synthesis of Mo-Cu nanocomposite powders[J].Journal of Alloys and Compounds,2011,509:L74-L77. |
| [4] | Aguilar, C.;Castro, F.;Martínez, V.;Guzmán, D.;de las Cuevas, F.;Lozada, L.;Vielma, N..Structural study of nanocrystalline solid solution of Cu-Mo obtained by mechanical alloying[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:189-194. |
| [5] | 陈玉柏,范景莲,刘涛,成会朝,田家敏.细晶钼铜合金的制备[J].中国有色金属学报,2008(06):1039-1044. |
| [6] | 李晓燕 .触头材料用铜合金电击穿性能研究[D].河南科技大学,2008. |
| [7] | 周贤良,叶志国,华小珍,张建云.熔渗和液相法烧结Mo-Cu合金的组织和性能[J].有色金属,2006(02):1-4. |
| [8] | 韩胜利,蔡一湘,宋月清,崔舜.制备工艺对Mo-Cu合金组织性能的影响[J].材料研究与应用,2010(02):100-105. |
| [9] | 张青花.Mo-Cu复合材料的最新研究进展[J].河西学院学报,2009(02):51-55. |
| [10] | 范景莲,陈玉柏,刘涛,田家敏.纳米晶Mo-Cu复合粉末烧结行为的研究[J].稀有金属材料与工程,2009(10):1693-1697. |
| [11] | 程继贵,弓艳飞,宋鹏,李洁.凝胶-共还原法制备超细Mo-Cu粉末及其烧结性能[J].中国有色金属学报,2007(03):422-427. |
| [12] | 田家敏,范景莲,陈玉柏,刘涛.细晶Mo-40%Cu合金的烧结性能[J].中南大学学报（自然科学版）,2010(05):1736-1742. |
| [13] | Aokui Sun;Xiaqjia Dong;Xiaoying Wang.Synthesis of novel core-shell Cu@Mo nanoparticles with good sinterability[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2013:6-9. |
| [14] | 王鹏飞,沈卫平,张强,张珂,蒋志明,陈鹏万.自蔓延预热爆炸固结Mo/Cu功能梯度材料的研究[J].稀有金属材料与工程,2007(04):652-655. |
| [15] | 奚正平;汤慧萍.烧结金属多孔材料[M].北京:冶金工业出版社,2009:2-95. |
| [16] | 李君强,陈文革,陶文俊,丁秉钧.W纤维增强高Cu含量W-Cu复合材料的研究[J].粉末冶金技术,2012(02):125-129. |
| [17] | Cho H;Kim HY;Kang JY;Kim TS .How the capillary burst microvalve works[J].Journal of Colloid and Interface Science,2007(2):379-385. |
| [18] | 夏扬,宋月清,崔舜,林晨光,韩胜利.Mo-Cu和W-Cu合金的制备及性能特点[J].稀有金属,2008(02):240-244. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%