采用溶胶-凝胶自燃烧法制得了柠檬酸盐络合物,该络合物经960℃煅烧7小时得到了纳米尺寸的Y2BaCuO5 (Y211)细粉.利用XRD对不同pH下的纳米尺寸Y211粉体特性如物相鉴定,晶粒尺寸,晶格常数等进行测量.实验发现干凝胶在空气中点燃后存在自蔓延燃烧.初始溶液中pH值影响了干凝胶自燃烧的过程,决定了自燃烧和煅烧粉体的晶格常数,密度,体积以及粒子尺寸.当pH =7,煅烧粉体的XRD图谱表明煅烧后粉体的平均晶粒尺寸(25nm)远小于自燃烧粉体的平均晶粒尺寸(48nm).此外,pH=5的煅烧粉体的晶格常数有一个最小值,而密度则达到了最大值6.224 g/cm3.
参考文献
| [1] | S. Hosseini Vajargah;H.R. Madaah Hosseini;Z.A. Nemati .Synthesis of nanocrystalline yttrium iron garnets by sol-gel combustion process: The influence of pH of precursor solution[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2006(1/3):211-215. |
| [2] | L. Rezlescu;E. Rezlescu .Fine barium hexaferrite powder prepared by the crystallisation of glass[J].Journal of Magnetism and Magnetic Materials,1999(1/3):288-290. |
| [3] | Guoqing Xu;Hongliang Ma;Minjian Zhong .Influence of pH on characteristics of BaFe_(12)O_(19) powder prepared by sol-gel auto-combustion[J].Journal of Magnetism and Magnetic Materials,2006(2):383-388. |
| [4] | 张辰,陈丽萍,王银博,吴桃李,刘文静,刘雨潇,薛驰,冯庆荣.溶胶凝胶法制备MgB2膜[J].低温物理学报,2011(02):97-102. |
| [5] | 鲁彦忠,孙爱民,刘恒伟,马耀通,马金元,艾小倩,张永福,孙丽娜,赵懂叶,马书懿.Y2Ba1Cu1O5-δ掺杂对Y1Ba2Cu3O7-δ的超导电性及其晶格结构的影响[J].低温物理学报,2011(06):450-453. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%